Shrinkage rate

TD:280°C,2.00mm2

ISO2577

%

0

Shrinkage rate

TD:120°C,4小时,2.00mm3

ISO2577

%

0

Shrinkage rate

MD:280°C,2.00mm2

ISO2577

%

0

Shrinkage rate

MD:120°C,4小时,2.00mm3

ISO2577

%

0

Tensile modulus

23°C

ISO527-2/1

Mpa

1

Tensile strain

断裂,23°C

ISO527-2/5

%

2

Tensile stress

断裂,23°C

ISO527-2/5

Mpa

1

Bending modulus 4

23°C

ISO178/A

Mpa

1

Bending strain 5

23°C

ISO178/A

%

2

Bending stress 4

23°C

ISO178/A

Mpa

2

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

2

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

2

Melting temperature 5

ISO11357-3

°C

2

Vicat softening temperature

ISO306/B120

°C

2

Linear coefficient of thermal expansion

MD：23到55°C

ISO11359-2

cm/cm/°C

2

Linear coefficient of thermal expansion

TD：23to55°C

ISO11359-2

cm/cm/°C

9

Surface resistivity

IEC60093

ohms

4

Leakage Trace Index

解决方案A

IEC60112

V

4

Volume resistivity

23°C

IEC60093

ohms·cm

3

Multi axis Instrumented Peak Impact Force

-30°C

ISO6603-2

N

9

Multi axis Instrumented Peak Impact Force

23°C

ISO6603-2

N

1

Multi axis Instrumented Impact Energy

-30°C

ISO6603-2

J

1

Multi axis Instrumented Impact Energy

23°C

ISO6603-2

J

3

Impact strength of simply supported beam without notch

-30°C

ISO179/1eU

kJ/m²

4

Impact strength of simply supported beam without notch

23°C

ISO179/1eU

kJ/m²

5

Unscented Izod impact strength

-30°C

ISO180/1U

kJ/m²

4

Unscented Izod impact strength

23°C

ISO180/1U

kJ/m²

5

Hot filament ignition temperature

0.40mm

IEC60695-2-13

°C

8

Hot filament ignition temperature

0.8mm

IEC60695-2-13

°C

7

Hot filament ignition temperature

1.5mm

IEC60695-2-13

°C

7

Hot filament ignition temperature

3.0mm

IEC60695-2-13

°C

8

Burning wire flammability index

0.40mm

IEC60695-2-12

°C

9

Burning wire flammability index

0.8mm

IEC60695-2-12

°C

9

Burning wire flammability index

1.5mm

IEC60695-2-12

°C

9

Burning wire flammability index

3.0mm

IEC60695-2-12

°C

9