Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP K65G2 BOREALIS EUROPE
XMOD™
Automotive sector
Thermal stability、High mobility、Recyclable、Glass fiber reinforced、Chemical coupling、Filler, fiberglass reinfo
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PP/BOREALIS EUROPE/K65G2
density
ISO1183
g/cm³
1
Melt mass flow rate
230°C/2.16kg
ISO1133
g/10min
6
Shrinkage rate
TD:2.00mm
ISO294-4
%
1
Shrinkage rate
MD:2.00mm
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PP/BOREALIS EUROPE/K65G2
Tensile modulus
1.00mm
ISO527-2
Mpa
5
Tensile strain
断裂
ISO527-2/50
%
3
Tensile stress
ISO527-2/50
Mpa
8
Bending modulus
ISO178
Mpa
4
Bending stress
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PP/BOREALIS EUROPE/K65G2
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Vicat softening temperature
--
ISO306/A
°C
1
Vicat softening temperature
--
ISO306/B
°C
1
Impact performance
Test Condition
Test Method
Unit
PP/BOREALIS EUROPE/K65G2
Charpy Notched Impact Strength
-20°C
ISO179/1eA
kJ/m²
7
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
8
Impact strength of simply supported beam without notch
-20°C
ISO179/1eU
kJ/m²
2
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
4
Impact strength of cantilever beam gap
23°C
ISO180/1A
kJ/m²
9
flammability
Test Condition
Test Method
Unit
PP/BOREALIS EUROPE/K65G2
atomization
100°C
DIN75201
mg
2