Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC SD-0150U LOTTE KOREA
STAREX®
Electrical applications
High mobility、High impact resistance、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/LOTTE KOREA/SD-0150U
Density/specific gravity
ASTMD792
g/cm³
1
Density/specific gravity
ISO1183
g/cm³
1
Melt mass flow rate
200°C/5.0kg
ASTMD1238
g/10min
1
Melt mass flow rate
200°C/5.0kg
ISO1133
g/10min
1
Shrinkage rate
MD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD：3.20mm
ASTMD955
%
0
Shrinkage rate
TD:3.20mm
ISO2577
%
0
Shrinkage rate
MD:3.20mm
ISO2577
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/LOTTE KOREA/SD-0150U
Tensile strength 2
屈服
ASTMD638
Mpa
4
Tensile strength 2
断裂
ASTMD638
Mpa
4
Tensile modulus
ISO527-2/50
Mpa
2
Tensile modulus 2
ASTMD638
Mpa
2
Tensile strain
断裂
ISO527-2/50
%
1
Tensile stress
屈服
ISO527-2/50
Mpa
4
Tensile stress
断裂
ISO527-2/50
Mpa
3
Elongation rate 2
断裂
ASTMD638
%
1
Bending modulus 3
ASTMD790
Mpa
2
Bending modulus 4
ISO178
Mpa
2
Bending strength 3
ASTMD790
Mpa
5
Bending stress 4
ISO178
Mpa
5
Thermal performance
Test Condition
Test Method
Unit
PC/LOTTE KOREA/SD-0150U
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
9
Hot deformation temperature
0.45MPa,Unannealed,4.00mm
ISO75-2/B
°C
9
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/A
°C
7
Vicat softening temperature
ISO306/B50
°C
9
Impact performance
Test Condition
Test Method
Unit
PC/LOTTE KOREA/SD-0150U
CharpyNotchedImpactStrength5
23°C
ISO179/1eA
kJ/m²
2
Impact strength of cantilever beam gap
23°C,3.18mm
ASTMD256
J/m
2
Impact strength of cantilever beam gap
23°C,6.35mm
ASTMD256
J/m
2
Suspended wall beam gap impact strength 5
23°C
ISO180/1A
kJ/m²
2
optical performance
Test Condition
Test Method
Unit
PC/LOTTE KOREA/SD-0150U
Huangdu Index
3.20mm
ASTMD1925
YI
1