Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 80G25HS BK117 DUPONT USA
Zytel®
Electronic and electrical、Automotive components
Resistance to oxidation、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA66/DUPONT USA/80G25HS BK117
Molding shrinkage rate
ASTM D955
%
0
physical property
Test Condition
Test Method
Unit
PA66/DUPONT USA/80G25HS BK117
Shrinkage rate
TD
ISO294-4
%
0
Shrinkage rate
MD
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA66/DUPONT USA/80G25HS BK117
elongation at break
ASTM D638/ISO 527
%
4
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
6
Tensile modulus
ISO527-2
Mpa
7
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
Tensile strain
断裂
ISO527-2
%
4
Tensile stress
断裂
ISO527-2
Mpa
1
Bending modulus
ISO178
Mpa
6
Bending modulus
ASTM D790/ISO 178
kg·cm/cm(J/M)ft·lb/in
6
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
2
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
8
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
8
Thermal performance
Test Condition
Test Method
Unit
PA66/DUPONT USA/80G25HS BK117
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature 2
ISO11357-3
°C
2
Impact performance
Test Condition
Test Method
Unit
PA66/DUPONT USA/80G25HS BK117
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
8
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
8
flammability
Test Condition
Test Method
Unit
PA66/DUPONT USA/80G25HS BK117
Burning rate 3
1.00mm
ISO3795
mm/min
<