Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC FXE1414 WH9D279 SABIC INNOVATIVE NANSHA
LEXAN™
Electrical appliances、Electronic field、Electrical field、Household appliances
Low temperature resistanc、transparent、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/FXE1414 WH9D279
Melt flow rate
300°C/1.2 kg
ASTM D1238
g/10 min
1
Molten Volume Flow Rate (MVR)
300°C/1.2 kg
ISO 1133
cm3/10min
9
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
9
300°C/1.2kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/FXE1414 WH9D279
Impact strength of simply supported beam gap
-30°C
ISO179/1eA
kJ/m²
6
Impact strength of simply supported beam gap
23°C
ISO179/1eA
kJ/m²
7
Impact strength of simply supported beam gap
-30°C
ISO 179/1eA
kJ/m²
6
Impact strength of simply supported beam gap
23°C
ISO 179/1eA
kJ/m²
7
Tensile strength
屈服 3
ASTM D638
Mpa
5
Tensile strength
屈服
ISO 527-2/50
Mpa
5
Tensile strength
断裂 3
ASTM D638
Mpa
5
Tensile strength
断裂
ISO 527-2/50
Mpa
6
Tensile strength
屈服
ASTMD638
Mpa
5
Tensile strength
断裂
ASTMD638
Mpa
5
Tensile modulus
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/1
Mpa
2
Tensile modulus
-- 2
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
Tensile strain
屈服
ISO527-2/50
%
6
Tensile strain
断裂
ISO527-2/50
%
1
Tensile stress
断裂
ISO527-2/50
Mpa
6
Tensile stress
屈服
ISO527-2/50
Mpa
5
Elongation rate
屈服
ASTMD638
%
6
Elongation rate
断裂
ASTMD638
%
9
elongation
屈服 3
ASTM D638
%
6
elongation
屈服
ISO 527-2/50
%
6
elongation
断裂 3
ASTM D638
%
9
elongation
断裂
ISO 527-2/50
%
1
Bending modulus
50.0 mm 跨距 4
ASTM D790
Mpa
2
Bending modulus
-- 5
ISO 178
Mpa
2
Bending modulus
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
Bending strength
屈服,50.0mm跨距
ASTMD790
Mpa
9
Bending strength 5,
ISO178
Mpa
8
Bending stress
-- 5, 6
ISO 178
Mpa
8
Bending stress
屈服, 50.0 mm 跨距 4
ASTM D790
Mpa
9
Suspended wall beam gap impact strength
-30°C
ISO180/1A
kJ/m²
6
Suspended wall beam gap impact strength
23°C
ISO180/1A
kJ/m²
7
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
7
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
7
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/FXE1414 WH9D279
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,Unannealed,100mmSpan
ISO75-2/Ae
°C
1
Vicat softening temperature
ASTMD152510
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Vicat softening temperature
--
ASTM D152510, ISO 306/B5010
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
流动 : 23 到 80°C
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : 23 到 80°C
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
MD：23到80°C
ISO11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：23to80°C
ISO11359-2
cm/cm/°C
7
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9
ISO 75-2/Ae
°C
1