Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM KFX-1003 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Electronic and electrical、Connector
High temperature resistan、Low temperature resistanc、Filler: Glass fiber reinf、10% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
POM/SABIC INNOVATIVE US/KFX-1003
Shrinkage rate
MD：24小时
ASTMD955
%
1
Shrinkage rate
TD：24hr
ASTMD955
%
1
Shrinkage rate
TD:24小时
ISO294-4
%
1
Shrinkage rate
MD:24小时
ISO294-4
%
1
Water absorption rate
24hr,50%RH
ASTMD570
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
POM/SABIC INNOVATIVE US/KFX-1003
Tensile strength
断裂
ASTMD638
Mpa
8
Tensile modulus
ISO527-2/1
Mpa
5
Tensile modulus 2
ASTMD638
Mpa
4
Tensile strain
断裂
ISO527-2
%
3
Tensile stress
断裂
ISO527-2
Mpa
8
elongation
断裂
ASTMD638
%
3
Bending modulus
ASTMD790
Mpa
4
Bending modulus
ISO178
Mpa
5
bending strength
ASTMD790
Mpa
1
Bending stress
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
POM/SABIC INNOVATIVE US/KFX-1003
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 4
1.8MPa,未退火,64.0mm跨距
ISO75-2/Af
°C
1
Impact performance
Test Condition
Test Method
Unit
POM/SABIC INNOVATIVE US/KFX-1003
UnnotchedIzodImpactStrength3
23°C
ISO180/1U
kJ/m²
3
Multi axis Instrumented Impact Energy
ISO6603-2
J
1
Suspended wall beam gap impact strength 3
23°C
ISO180/1A
kJ/m²
5