Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC SC-1100R LOTTE KOREA
INFINO®
Electrical field、Electronic field、Industrial components、Industrial applications、Automotive sector、Automotive interior parts、Automotive External Parts
currency、High temperature resistan、transparent、Flame retardant、Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/LOTTE KOREA/SC-1100R
Melt flow rate
300°C/1.2 kg
ASTM D1238, ISO 1133
g/10 min
1
Shrinkage rate
流动 : 3.20 mm
ASTM D955
%
0
Shrinkage rate
横向流动 : 3.20 mm
ASTM D955
%
0
Shrinkage rate
横向流量 : 2.00 mm
ISO 294-4
%
0
Shrinkage rate
流量 : 2.00 mm
ISO 294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/LOTTE KOREA/SC-1100R
Tensile strength
屈服 3
ASTM D638
Mpa
6
Tensile strength
屈服
ISO 527-2/50
Mpa
6
Tensile strength
断裂 3
ASTM D638
Mpa
6
Tensile strength
断裂
ISO 527-2/50
Mpa
6
Tensile modulus
-- 3
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/50
Mpa
2
elongation
断裂 3
ASTM D638
%
1
elongation
断裂
ISO 527-2/50
%
1
Bending modulus
-- 4
ASTM D790
Mpa
2
Bending modulus
-- 5
ISO 178
Mpa
2
bending strength
-- 4
ASTM D790
Mpa
9
bending strength
-- 5
ISO 178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/LOTTE KOREA/SC-1100R
Vicat softening temperature
ISO 306/B50
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm
ISO 75-2/B
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm
ISO 75-2/A
°C
1