Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 41H ASCEND USA
Vydyne®
--
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/ASCEND USA/41H
Shrinkage rate
横向流量 : 2.00 mm
ISO 294-4
%
1
Shrinkage rate
流量 : 2.00 mm
ISO 294-4
%
1
Mechanical performance
Test Condition
Test Method
Unit
PA66/ASCEND USA/41H
Tensile modulus
23°C
ISO 527-2
Mpa
1
Tensile strain
断裂, 23°C
ISO 527-2
%
5
Tensile stress
屈服, 23°C
ISO 527-2
Mpa
4
Tensile stress
断裂, 23°C
ISO 527-2
Mpa
4
Bending modulus
23°C
ISO 178
Mpa
1
Bending stress
23°C
ISO 178
Mpa
5
Thermal performance
Test Condition
Test Method
Unit
PA66/ASCEND USA/41H
RTI
0.75 mm
UL 746
°C
1
RTI
1.5 mm
UL 746
°C
1
RTI
3.0 mm
UL 746
°C
1
RTI Elec
0.75 mm
UL 746
°C
1
RTI Elec
1.5 mm
UL 746
°C
1
RTI Elec
3.0 mm
UL 746
°C
1
RTI Imp
0.75 mm
UL 746
°C
7
RTI Imp
1.5 mm
UL 746
°C
7
RTI Imp
3.0 mm
UL 746
°C
7
Hot deformation temperature
1.8 MPa, 未退火
ISO 75-2/A
°C
5
Melting temperature
ISO 11357-3
°C
2
Linear coefficient of thermal expansion
流动 : 23 到 55°C, 2.00 mm
ISO 11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
横向 : 23 到 55°C, 2.00 mm
ISO 11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PA66/ASCEND USA/41H
Dielectric strength
1.00 mm
IEC 60243
KV/mm
1
Leakage Trace Index
3.00 mm
IEC 60112
V
6
Volume resistivity
0.750 mm
IEC 60093
ohms·cm
1
flammability
Test Condition
Test Method
Unit
PA66/ASCEND USA/41H
Burning rate
2.00 mm
ISO 3795
mm/min
1
Burning rate
3.00 mm
ISO 3795
mm/min
7
Hot filament ignition temperature
0.75 mm
IEC 60695-2-13
°C
7
Hot filament ignition temperature
1.5 mm
IEC 60695-2-13
°C
7
Hot filament ignition temperature
3.0 mm
IEC 60695-2-13
°C
7
Burning wire flammability index
0.75 mm
IEC 60695-2-12
°C
7
Burning wire flammability index
1.5 mm
IEC 60695-2-12
°C
7
Burning wire flammability index
3.0 mm
IEC 60695-2-12
°C
6