Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI JL-4030 BK SABIC INNOVATIVE US
ULTEM™
Electronic and electrical
Hydrolysis resistance、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/JL-4030 BK
Shrinkage rate
MD：24小时
ASTMD955
%
0
Shrinkage rate
TD：24hr
ASTMD955
%
0
Shrinkage rate
TD:24小时
ISO294-4
%
0
Shrinkage rate
MD:24小时
ISO294-4
%
0
Water absorption rate
24hr,50%RH
ASTMD570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/JL-4030 BK
Tensile strength
断裂
ASTMD638
Mpa
5
Tensile strain
断裂
ISO527-2
%
1
Tensile stress
断裂
ISO527-2
Mpa
5
Wear factor - Washer
ASTMD3702Modified
10^-10in^5-min/ft-lb-hr
2
elongation
断裂
ASTMD638
%
9
Bending modulus
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
bending strength
ASTMD790
Mpa
7
Bending stress
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/JL-4030 BK
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 3
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
1
Hot deformation temperature 3
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
1
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE US/JL-4030 BK
UnnotchedIzodImpactStrength2
23°C
ISO180/1U
kJ/m²
5
Suspended wall beam notch impact strength 2
23°C
ISO180/1A
kJ/m²
6