Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS G-10 BK TOSOH JAPAN
SUSTEEL®
Electrical field、Electronic field、Automotive sector、Lighting fixtures
Glass fiber reinforced、enhance、Filler: Glass mineral
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPS/TOSOH JAPAN/G-10 BK
Melt mass flow rate
315°C/5.0kg
ASTMD1238
g/10min
9
Shrinkage rate
MD
内部方法
%
0
Shrinkage rate
TD
内部方法
%
0
Water absorption rate
平衡
ASTMD570
%
>
Mechanical performance
Test Condition
Test Method
Unit
PPS/TOSOH JAPAN/G-10 BK
Tensile Weld Strength
ASTMD638
Mpa
3
Charpy impact strength
有缺口
ASTM D-256
J/m
6
Charpy impact strength
无缺口
ASTM D-256
J/m
2
Tensile strength
ASTMD638
Mpa
1
tensile strength
ASTM D-638
Mpa
1
elongation
断裂
ASTMD638
%
0
Bending modulus
ASTMD790
Mpa
2
Bending modulus
ASTM D-790
GPa
2
bending strength
ASTM D-790
Mpa
2
bending strength
ASTMD790
Mpa
2
Elongation rate
ASTM D-638
%
0
Thermal performance
Test Condition
Test Method
Unit
PPS/TOSOH JAPAN/G-10 BK
Hot deformation temperature
1.82MPa
ASTM D-648
°C
＞
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
>
Melting temperature
内部方法
°C
2
Electrical performance
Test Condition
Test Method
Unit
PPS/TOSOH JAPAN/G-10 BK
Dielectric breakdown strength
ASTM D-149
KV/mm
1
Dielectric strength
ASTMD149
KV/mm
1
Arc resistance
ASTMD495
sec
1
Thermal conductivity
自定标准
W/m.K
0
Volume resistivity
ASTMD257
ohms·cm
1
Volume resistance value
ASTM D-257
Ω.cm
4
Processing performance
Test Condition
Test Method
Unit
PPS/TOSOH JAPAN/G-10 BK
Shrinkage rate
垂直方向
ASTM D-955
%
0
Shrinkage rate
流动方向
ASTM D-955
%
0
Impact performance
Test Condition
Test Method
Unit
PPS/TOSOH JAPAN/G-10 BK
Cantilever beam without notch impact strength
ASTMD256
J/m
2
Supplementary Information
Test Condition
Test Method
Unit
PPS/TOSOH JAPAN/G-10 BK
BarFlowLength
1.00mm
内部方法
mm
1