Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT X5630P SABIC INNOVATIVE US
XENOY™
Automotive Applications
High mobility、High impact resistance、Dimensional stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X5630P
Molten Volume Flow Rate (MVR)
265°C/5.0 kg
ISO 1133
cm3/10min
1
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X5630P
Tensile modulus
ISO 527-2/1
Mpa
4
Tensile strain
断裂
ISO 527-2/5
%
8
Tensile strain
屈服
ISO 527-2/5
%
3
Tensile stress
断裂
ISO 527-2/5
Mpa
5
Tensile stress
屈服
ISO 527-2/5
Mpa
5
Bending modulus 1
ISO 178
Mpa
4
Bending stress 1, 2
ISO 178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X5630P
Hot deformation temperature
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距
ISO 75-2/Af
°C
1
Vicat softening temperature
--
ISO 306/B120
°C
1
Vicat softening temperature
--
ISO 306/B50
°C
1
Linear coefficient of thermal expansion
横向 : -30 到 80°C
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
流动 : -30 到 80°C
ISO 11359-2
cm/cm/°C
5
Impact performance
Test Condition
Test Method
Unit
PC/PBT/SABIC INNOVATIVE US/X5630P
Unscented Izod Impact Strength 4
23°C
ISO 180/1U
kJ/m²
1
Unscented Izod Impact Strength 4
-30°C
ISO 180/1U
kJ/m²
8
Suspended wall beam gap impact strength 4
23°C
ISO 180/1A
kJ/m²
8
Suspended wall beam gap impact strength 4
-30°C
ISO 180/1A
kJ/m²
6