PC LDS 3730/13701 MITSUBISHI ENGINEERING JAPAN
IUPILON™
Laser beacon、Phone
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/LDS 3730/13701
Melt volume flow rate
260°C/5.0kg
ISO1133
cm3/10min
1
Shrinkage rate
MD
ISO294-4
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/LDS 3730/13701
Nominal tensile fracture strain
ISO527-2
%
>
Tensile modulus
ISO527-2
Mpa
2
Tensile strain
屈服
ISO527-2
%
5
Tensile stress
屈服
ISO527-2
Mpa
5
Bending modulus
ISO178
Mpa
2
Bending stress
ISO178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/LDS 3730/13701
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Vicat softening temperature
ISO306/B50
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
6
Electrical performance
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/LDS 3730/13701
Surface resistivity
IEC60093
ohms
>
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/MITSUBISHI ENGINEERING JAPAN/LDS 3730/13701
Multi axis Instrumented Impact Energy
-20°C2
内部方法
J
2
Multi axis Instrumented Impact Energy
23°C
ISO6603-2
J
3
Multi axis Instrumented Impact Energy
23°C2
内部方法
J
2