Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA9T TA124 KURARAY JAPAN
Genestar™
--
Filler, mineral filler, 3
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA9T/KURARAY JAPAN/TA124
density
ISO1183
g/cm³
1
Melt mass flow rate
230°C/2.16kg
ISO1133
g/10min
2
Melt mass flow rate
230°C/5.0kg
ISO1133
g/10min
1
Shrinkage rate
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA9T/KURARAY JAPAN/TA124
Tensile modulus
ISO527-2/1
Mpa
2
Tensile strain
屈服
ISO527-2/50
%
5
Tensile stress
屈服
ISO527-2/50
Mpa
2
Bending modulus
ISO178
Mpa
3
Bending stress
ISO178
Mpa
4
Thermal performance
Test Condition
Test Method
Unit
PA9T/KURARAY JAPAN/TA124
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
6
Vicat softening temperature
--
ISO306/A50
°C
1
Vicat softening temperature
--
ISO306/B50
°C
8
Impact performance
Test Condition
Test Method
Unit
PA9T/KURARAY JAPAN/TA124
Charpy Notched Impact Strength
-20°C
ISO179/1eA
kJ/m²
1
Charpy Notched Impact Strength
23°C
ISO179/1eA
kJ/m²
4
Impact strength of simply supported beam without notch
-20°C
ISO179/1eU
kJ/m²
1
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
5
hardness
Test Condition
Test Method
Unit
PA9T/KURARAY JAPAN/TA124
Ball pressure hardness
H358/30
ISO2039-1
Mpa
7