Shrinkage rate

TD

ISO294-4

%

0

Shrinkage rate

MD

ISO294-4

%

0

Water absorption rate

饱和,23°C

ISO62

%

5

Fracture bending strain

ISO178

%

1

Tensile modulus

ISO527-2/1A/1

Mpa

1

Tensile strain

断裂

ISO527-2/1A/5

%

1

Tensile stress

断裂

ISO527-2/1A/5

Mpa

1

Bending modulus

23°C

ISO178

Mpa

1

Bending stress

23°C

ISO178

Mpa

1

Compressive modulus

ISO604

Mpa

1

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

2

Melting temperature 3

ISO11357-3

°C

3

Vicat softening temperature

ISO306/B50

°C

2

Linear coefficient of thermal expansion

MD

ISO11359-2

cm/cm/°C

8

Linear coefficient of thermal expansion

TD

ISO11359-2

cm/cm/°C

4

Surface resistivity

IEC60093

ohms

1

Dielectric strength

IEC60243-1

KV/mm

5

Leakage Trace Index

IEC60112

V

1

Volume resistivity

IEC60093

ohms·cm

1

Impact strength of simply supported beam without notch

23°C

ISO179/1eU

kJ/m²

2

Unscented Izod impact strength

23°C

ISO180/1U

kJ/m²

2