Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO PVX0901 BK1066 SABIC INNOVATIVE SHANGHAI
NORYL™
office equipment 、Home appliance components、Automotive Applications、currency
High temperature resistan、Hydrolysis resistance、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/PVX0901 BK1066
Melt volume flow rate
280°C/5.0kg
ISO1133
cm3/10min
5
Melt mass flow rate
280°C/5.0kg
ASTMD1238
g/10min
5
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/PVX0901 BK1066
Tensile strength
屈服4
ASTMD638
Mpa
6
Tensile strength
屈服
ISO527-2/50
Mpa
5
Tensile strength
断裂4
ASTMD638
Mpa
4
Tensile strength
断裂
ISO527-2/50
Mpa
4
Tensile modulus
--3
ASTMD638
Mpa
2
Tensile modulus
--
ISO527-2/1
Mpa
2
elongation
断裂4
ASTMD638
%
6
elongation
断裂
ISO527-2/50
%
8
elongation
屈服4
ASTMD638
%
3
elongation
屈服
ISO527-2/50
%
3
Bending modulus
50.0mm跨距5
ASTMD790
Mpa
2
Bending modulus
--6
ISO178
Mpa
2
Bending stress
--6,7
ISO178
Mpa
9
Bending stress
屈服,50.0mm跨距5
ASTMD790
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/PVX0901 BK1066
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
9
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
9
Hot deformation temperature
1.8MPa,未退火,64.0mm跨距10
ISO75-2/Af
°C
8
Vicat softening temperature
--
ASTMD152511,ISO306/B5011
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831
cm/cm/°C
7
Linear coefficient of thermal expansion
MD:-40到40°C
ISO11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831
cm/cm/°C
8
Linear coefficient of thermal expansion
TD:-40到40°C
ISO11359-2
cm/cm/°C
7
Impact performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/PVX0901 BK1066
Impact strength of simply supported beam gap 8
23°C
ISO179/1eA
kJ/m²
1
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
3