Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI 2312-1000 SABIC INNOVATIVE SHANGHAI
ULTEM™
Electrical tools、Automotive Applications
High temperature resistan、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE SHANGHAI/2312-1000
Melt flow rate
337°C/6.6 kg
ASTM D1238
g/10 min
1
Shrinkage rate
流动 : 3.20 mm
内部方法
%
0
Shrinkage rate
横向流动 : 3.20 mm
内部方法
%
0
Water absorption rate
24 hr
ASTM D570
%
0
Water absorption rate
平衡, 23°C
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE SHANGHAI/2312-1000
Tensile strength
断裂
ASTM D638
Mpa
1
Tensile modulus 1
ASTM D638
Mpa
5
elongation
断裂
ASTM D638
%
3
Bending modulus
100 mm 跨距
ASTM D790
Mpa
6
bending strength
断裂, 100 mm 跨距
ASTM D790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE SHANGHAI/2312-1000
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
Linear coefficient of thermal expansion
流动 : -20 到 150°C
ASTM E831
cm/cm/°C
2
Linear coefficient of thermal expansion
横向 : -20 到 150°C
ASTM E831
cm/cm/°C
2
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
2
Impact performance
Test Condition
Test Method
Unit
PEI/SABIC INNOVATIVE SHANGHAI/2312-1000
Reverse notch impact
3.20 mm
ASTM D256
J/m
3