Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM/PTFE FL2010 MITSUBISHI ENGINEERING JAPAN
Iupital™
Electronic and Electrical、Automotive sector
Weather resistance、Medium viscosity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
POM/PTFE/MITSUBISHI ENGINEERING JAPAN/FL2010
Melt volume flow rate
190°C/2.16kg
ISO1133
cm3/10min
6
Melt mass flow rate
190°C/2.16kg
ISO1133
g/10min
7
Water absorption rate 1
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
POM/PTFE/MITSUBISHI ENGINEERING JAPAN/FL2010
Nominal tensile fracture strain
ISO527-2
%
1
Tensile modulus
ISO527-2
Mpa
2
Tensile strain
屈服
ISO527-2
%
8
Tensile stress
屈服
ISO527-2
Mpa
5
Bending modulus
ISO178
Mpa
2
Bending stress
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
POM/PTFE/MITSUBISHI ENGINEERING JAPAN/FL2010
0.45MPa, unannealed
ISO75-2/B
°C
1
1.8MPa, unannealed
ISO75-2/A
°C
9
Melting temperature
ISO11357-3
°C
1
Linear coefficient of thermal expansion
MD
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD
ISO11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
POM/PTFE/MITSUBISHI ENGINEERING JAPAN/FL2010
Surface resistivity
IEC60093
ohms
1
Dielectric strength
1.00mm
IEC60243-1
KV/mm
2
Dielectric strength
3.00mm
IEC60243-1
KV/mm
1
Leakage Trace Index
IEC60112
V
6
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
POM/PTFE/MITSUBISHI ENGINEERING JAPAN/FL2010
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
6