Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO N1250 BK1066 SABIC INNOVATIVE SHANGHAI
NORYL™
Electrical applications、Automotive interior parts
High temperature resistan、High mobility、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/N1250 BK1066
Melt flow rate
300°C/5.0 kg
ASTM D1238
g/10 min
2
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/N1250 BK1066
Tensile strength 3
屈服
ASTM D638
Mpa
7
Tensile strength 3
断裂
ASTM D638
Mpa
6
Tensile modulus 2
ASTM D638
Mpa
2
Elongation rate 3
屈服
ASTM D638
%
4
Elongation rate 3
断裂
ASTM D638
%
2
Bending modulus
50.0 mm 跨距
ASTM D790
Mpa
2
bending strength
屈服, 50.0 mm 跨距
ASTM D790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/N1250 BK1066
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
Vicat softening temperature
ASTM D15255
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
6
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
6
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Impact performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/N1250 BK1066
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
4