Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 855-1001 SABIC INNOVATIVE SHANGHAI
VALOX™
Electrical field、Electrical appliances、Electronic field、Electronic display、Construction field、Medical supplies、Lighting applications
Excellent appearance、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE SHANGHAI/855-1001
Melt flow rate
266°C/5.0 kg
ASTM D1238
g/10 min
7
Shrinkage rate
横向流动 : 3.20 到 4.60 mm
内部方法
%
0
Shrinkage rate
横向流动 : 1.50 到 3.20 mm
内部方法
%
0
Shrinkage rate
流动 : 3.20 到 4.60 mm
内部方法
%
0
Shrinkage rate
流动 : 1.50 到 3.20 mm
内部方法
%
0
Specific volume
ASTM D792
cm³/g
0
Water absorption rate
24 hr
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE SHANGHAI/855-1001
Tensile strength
断裂
ASTM D638
Mpa
9
Bending modulus
50.0 mm 跨距
ASTM D790
Mpa
5
bending strength
断裂, 50.0 mm 跨距
ASTM D790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE SHANGHAI/855-1001
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
Linear coefficient of thermal expansion - flow
60 到 138°C
ASTM E831
cm/cm/°C
6
Linear coefficient of thermal expansion - flow
-40 到 40°C
ASTM E831
cm/cm/°C
4
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
2
Electrical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE SHANGHAI/855-1001
Dielectric strength
3.20 mm, in Air
ASTM D149
KV/mm
2
Dielectric strength
1.60 mm, in Oil
ASTM D149
KV/mm
2
Volume resistivity
ASTM D257
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE SHANGHAI/855-1001
Non notched cantilever beam impact
23°C
ASTM D4812
J/m
3