Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS FR15U SABIC INNOVATIVE US
CYCOLAC™
Automotive sector、Electronic field、Electrical field
Flame retardant、UV resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/FR15U
MeltViscosity
200°C,1000sec^-1
ASTMD3835
Pa·s
3
Density/specific gravity
ASTMD792
g/cm³
1
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
220°C/10.0kg
ISO1133
cm3/10min
4
230°C/3.8kg
ASTMD1238
g/10min
3
220°C/5.0kg
ISO1133
g/10min
7
Shrinkage rate
MD：3.20mm
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/FR15U
NotchedIzodImpactStrength
23°C
ISO180/1A
kJ/m²
1
Tensile strength
断裂
ASTMD638
Mpa
3
Tensile strength
屈服
ASTMD638
Mpa
3
Tensile modulus
ASTMD638
Mpa
2
Tensile modulus
ISO527-2/1
Mpa
2
Tensile strain
断裂
ISO527-2/50
%
2
Tensile stress
屈服
ISO527-2/50
Mpa
4
Elongation rate
屈服
ASTMD638
%
2
Elongation rate
断裂
ASTMD638
%
1
Bending modulus
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus
ISO178
Mpa
2
Bending strength
屈服,50.0mm跨距
ASTMD790
Mpa
6
Bending strength 5,
ISO178
Mpa
6
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
2
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
2
Thermal performance
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/FR15U
RTIElec
UL746
°C
9
Evolution Calendar intelligent importer
UL746
°C
8
RTIStr
UL746
°C
9
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
7
Vicat softening temperature
ASTMD15258
°C
9
Vicat softening temperature
ISO306/B50
°C
9
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
9
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
9
Electrical performance
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/FR15U
Dielectric strength
3.20mm,在油中
IEC60243-1
KV/mm
2
Volume resistivity
IEC60093
ohms·cm
>