Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT ENH4530 SABIC INNOVATIVE NANSHA
VALOX™
Electronic display、Automotive External Parts
Flame retardant、Bromine free、Chlorine free、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/ENH4530
Melt volume flow rate
250°C/5.0kg
ISO1133
cm3/10min
1
Melt volume flow rate
265°C/5.0kg
ISO1133
cm3/10min
1
Melt mass flow rate
265°C/5.0kg
ASTMD1238
g/10min
2
Shrinkage rate
MD1
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/ENH4530
--
ISO527-2/1
Mpa
7
--2
ASTMD638
Mpa
7
50.0mm span 7
ASTMD790
Mpa
5
--8
ISO178
Mpa
6
--9
ISO178
Mpa
1
crack
ISO527-2/5
%
3
crack
ISO527-2/5
Mpa
8
Fracture, 50.0mm span 11
ASTMD790
Mpa
1
Fracture 4
ASTMD638
Mpa
8
Fracture 6
ASTMD638
%
3
Fracture bending strain 12
ISO178
%
3
yield
ISO527-2/5
%
2
yield
ISO527-2/5
Mpa
8
Yield, 50.0mm span of 10
ASTMD790
Mpa
1
Surrender 3
ASTMD638
Mpa
8
Surrender 5
ASTMD638
%
2
Thermal performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/ENH4530
--
ISO306/A50
°C
2
--
ASTMD1525,ISO306/B50,ISO306/B12020
°C
2
--
ASTMD152521
°C
2
0.45MPa, unannealed, 3.20mm
ASTMD648
°C
2
0.45MPa, unannealed, 64.0mm span 18
ISO75-2/Bf
°C
2
1.8MPa, unannealed, 3.20mm
ASTMD648
°C
2
1.8MPa, unannealed, 64.0mm span 19
ISO75-2/Af
°C
2
RTI
UL746
°C
1
RTIElec
UL746
°C
1
Evolution Calendar intelligent importer
UL746
°C
1
Linear coefficient of thermal expansion
MD:-40到40°C
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
MD:23到150°C
ISO11359-2
cm/cm/°C
4
Linear coefficient of thermal expansion
TD:-40到40°C
ISO11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
TD:23到150°C
ISO11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/ENH4530
0.800mm,inOil
ASTMD149
KV/mm
2
0.800mm, in oil
IEC60243-1
KV/mm
2
1.60mm,inOil
ASTMD149
KV/mm
2
1.60mm, in oil
IEC60243-1
KV/mm
2
3.20mm, inoil
ASTMD149
KV/mm
1
3.20mm, in oil
IEC60243-1
KV/mm
1
Surface resistivity
IEC60093
ohms
>
Volume resistivity
ASTMD257,IEC60093
ohms·cm
1
Filling analysis
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/ENH4530
Melt viscosity
260°C,1500sec^-1
ISO11443
Pa·s
1
Impact performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/ENH4530
0°C
ASTMD256
J/m
5
0°C14
ISO180/1A
kJ/m²
6
23°C
ASTMD4812
J/m
4
23°C
ASTMD256
J/m
5
23°C15
ISO180/1A
kJ/m²
6
23°C17
ISO180/1U
kJ/m²
3
-30°C
ASTMD256
J/m
5
-30°C
ASTMD4812
J/m
3
-30°C13
ISO180/1A
kJ/m²
6
-30°C16
ISO180/1U
kJ/m²
2
Impact strength of simply supported beam without notch
-30°C
ISO179/2U
kJ/m²
2
Impact strength of simply supported beam without notch
23°C
ISO179/2U
kJ/m²
3
hardness
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/ENH4530
Ball pressure hardness
H358/30
ISO2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/ENH4530
Hot filament ignition temperature
3.00mm
IEC60695-2-13
°C
7
Burning wire flammability index
3.00mm
IEC60695-2-12
°C
9
Supplementary Information
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/ENH4530
Filling material
ASTMD229
%
1