PBT 3300 JAPAN POLYPLASTIC
DURANEX®
Automotive sector
Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/3300
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/3300
IZOD impact strength (with notch)
缺口侧
ASTM D-256
J/m
9
IZOD impact strength (with notch)
反缺口侧
ASTM D-256
J/m
5
elongation at break
ASTM D638/ISO 527
%
2
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
tensile strength
ASTM D-638
Mpa
1
Tensile strain
断裂
ISO527-2
%
2
Tensile stress
ISO527-2
Mpa
1
elongation
ASTM D-638
%
2
Bending modulus
ISO178
Mpa
9
Bending modulus
ASTM D-790
Mpa
9
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
9
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D-790
Mpa
2
Bending stress
ISO178
Mpa
2
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
9
Thermal performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/3300
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Hot deformation temperature
1.82MPa
ASTM D-648
°C
2
Linear coefficient of thermal expansion
MD：23到55°C
内部方法
cm/cm/°C
2
Linear coefficient of thermal expansion
TD：23to55°C
内部方法
cm/cm/°C
9
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
2
Electrical performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/3300
Dielectric breakdown strength
2mmt
ASTM D-149
MV/m
2
Dielectric strength
3.00mm
IEC60243-1
KV/mm
2
Leakage Trace Index
IEC60112
V
3
Volume resistivity
IEC60093
ohms·cm
5
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
5
Volume resistivity
3mmt
ASTM D-257
Ω.cm
5