Melt volume flow rate

250°C/2.16kg

ISO1133

cm3/10min

9

Melt volume flow rate

250°C/5.0kg

ISO1133

cm3/10min

2

Shrinkage rate

MD

内部方法

%

0

Shrinkage rate

TD

内部方法

%

0

Water absorption rate

饱和,23°C

ISO62

%

0

Water absorption rate

平衡,23°C,50%RH

ISO62

%

0

Tensile modulus

ISO527-2/1

Mpa

2

Tensile strain

屈服

ISO527-2/50

%

5

Tensile strain

断裂

ISO527-2/50

%

1

Tensile stress

屈服

ISO527-2/50

Mpa

5

Tensile stress

断裂

ISO527-2/50

Mpa

4

Taber abraser

1000Cycles,1000g,CS-17转轮

内部方法

mg

3

Bending modulus 2

ISO178

Mpa

2

Bending stress 3

ISO178

Mpa

7

--

ISO306/A50

°C

1

--

ISO306/B50

°C

1

--

ISO306/B120

°C

1

0.45MPa, unannealed, 100mm span

ISO75-2/Be

°C

1

1.8MPa, unannealed, 100mm span

ISO75-2/Ae

°C

8

thermal conductivity

ISO8302

W/m/K

0

Linear coefficient of thermal expansion

MD:23到80°C

ISO11359-2

cm/cm/°C

1

Linear coefficient of thermal expansion

TD:23到80°C

ISO11359-2

cm/cm/°C

1

Surface resistivity

IEC60093

ohms

>

Dielectric strength

0.800mm,在油中

IEC60243-1

KV/mm

3

Dielectric strength

1.60mm,在油中

IEC60243-1

KV/mm

2

Dielectric strength

3.20mm,在油中

IEC60243-1

KV/mm

1

Volume resistivity

IEC60093

ohms·cm

>

Impact strength of simply supported beam gap 4

-30°C

ISO179/1eA

kJ/m²

2

Impact strength of simply supported beam gap 4

23°C

ISO179/1eA

kJ/m²

5

Suspended wall beam notch impact strength 6

-30°C

ISO180/1A

kJ/m²

1

Suspended wall beam notch impact strength 6

23°C

ISO180/1A

kJ/m²

4

Ball pressure hardness

H358/30

ISO2039-1

Mpa

1

Burning wire flammability index

3.20mm

IEC60695-2-12

°C

7