Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3 GF 30 AKRO-PLASTIC GERMANY
AKROMID®
Engineering accessories、Industrial applications、Automotive sector、Application in the automo
enhance、Thermal stability、30%、Filler by weight、Filler: Glass fiber reinf
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA66/AKRO-PLASTIC GERMANY/A3 GF 30
HumidityAbsorption-62%RH
70°C
ISO1110
%
1
Shrinkage rate
TD
ISO294-4
%
1
Shrinkage rate
MD
ISO294-4
%
0
Water absorption rate
饱和,23°C
ISO62
%
5
Mechanical performance
Test Condition
Test Method
Unit
PA66/AKRO-PLASTIC GERMANY/A3 GF 30
Tensile modulus
ISO527-2/1
Mpa
9
Tensile strain
断裂
ISO527-2/5
%
3
Tensile stress
断裂
ISO527-2/5
Mpa
1
Bending modulus 2
ISO178
Mpa
8
Bending stress 2
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA66/AKRO-PLASTIC GERMANY/A3 GF 30
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Hot deformation temperature
8.0MPa,未退火
ISO75-2/C
°C
2
Melting temperature 5
DINEN11357-1
°C
2
Linear coefficient of thermal expansion
MD：23到80°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：23to80°C
ISO11359-2
cm/cm/°C
9
Impact performance
Test Condition
Test Method
Unit
PA66/AKRO-PLASTIC GERMANY/A3 GF 30
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
8
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
8
flammability
Test Condition
Test Method
Unit
PA66/AKRO-PLASTIC GERMANY/A3 GF 30
Burning rate 4
1.00mm
FMVSS302
mm/min
<
Supplementary Information
Test Condition
Test Method
Unit
PA66/AKRO-PLASTIC GERMANY/A3 GF 30
ReinforcementContent
ISO1172
%
3