Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS FR23-NA1000 SABIC INNOVATIVE US
CYCOLAC™
Automotive Applications
High mobility、flexibility、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/FR23-NA1000
Melt flow rate
230°C/3.8 kg
ASTM D1238
g/10 min
6
Melt flow rate
220°C/5.0 kg
ISO 1133
g/10 min
9
Molten Volume Flow Rate (MVR)
220°C/10.0 kg
ISO 1133
cm3/10min
3
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/FR23-NA1000
Tensile strength 3
屈服
ASTM D638
Mpa
4
Tensile strength 3
断裂
ASTM D638
Mpa
3
Tensile modulus 2
ASTM D638
Mpa
2
Elongation rate 3
屈服
ASTM D638
%
2
Elongation rate 3
断裂
ASTM D638
%
1
Bending modulus
50.0 mm 跨距
ASTM D790
Mpa
2
bending strength
屈服, 50.0 mm 跨距
ASTM D790
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/FR23-NA1000
RTI
UL 746
°C
6
RTI Elec
UL 746
°C
6
RTI Imp
UL 746
°C
6
Vicat softening temperature
ASTM D15255
°C
9
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
8
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
7
Filling analysis
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/FR23-NA1000
Melt viscosity
200°C, 1000 sec^-1
ASTM D3835
Pa·s
3
Impact performance
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/FR23-NA1000
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
4