Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 S RV150 100 NA RADIC ITALY
RADILON®
--
Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA6/RADIC ITALY/S RV150 100 NA
Shrinkage rate
TD
ISO294-4
%
0
Shrinkage rate
MD
ISO294-4
%
0
Water absorption rate
饱和,23°C,2.00mm
ISO62
%
8
Water absorption rate
平衡,23°C,2.00mm,50%RH
ISO62
%
2
Mechanical performance
Test Condition
Test Method
Unit
PA6/RADIC ITALY/S RV150 100 NA
Nominal tensile fracture strain
ISO527-2/1A/50
%
-
Tensile modulus
ISO527-2/1A/1
Mpa
5
Tensile strain
屈服
ISO527-2/1A/50
%
-
Tensile strain
断裂
ISO527-2/1A/5
%
3
Tensile stress
屈服
ISO527-2/1A/50
Mpa
-
Tensile stress
断裂
ISO527-2/1A/5
Mpa
1
Bending modulus 3
ISO178
Mpa
5
Bending stress 3
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PA6/RADIC ITALY/S RV150 100 NA
Hot deformation temperature
1.8MPa,未退火
ISO75-2/Af
°C
1
Melting temperature 5
ISO11357
°C
2
Vicat softening temperature
ISO306/B50
°C
2
Electrical performance
Test Condition
Test Method
Unit
PA6/RADIC ITALY/S RV150 100 NA
Surface resistivity
IEC60093
ohms
1
Leakage Trace Index
IEC60112
V
6
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PA6/RADIC ITALY/S RV150 100 NA
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
4
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
4
flammability
Test Condition
Test Method
Unit
PA6/RADIC ITALY/S RV150 100 NA
Burning rate
FMVSS302
mm/min
0
Burning wire flammability index
2.0mm
IEC60695-2-12
°C
7