Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 420SE0-1001 SABIC INNOVATIVE JAPAN
VALOX™
Lawn equipment、Electrical field、Electrical appliances、Electronic field、Electronic display、Engine hood parts、Textile application、Industrial applications、Nursing supplies、Household goods、Architectural application、Automotive interior parts、Automotive External Parts、Petroleum Applications、Outdoor applications、sporting goods、Natural gas supplies、Medical supplies、Garden equipment、Lighting fixtures、Lighting applications
Glass fiber reinforced、dimensional stability 、High rigidity、high strength、heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE JAPAN/420SE0-1001
Melt flow rate
250°C/5.0 kg
ASTM D1238
g/10 min
4
Molten Volume Flow Rate (MVR)
250°C/5.0 kg
ISO 1133
cm3/10min
2
Shrinkage rate
流动 2
内部方法
%
0
Shrinkage rate
流动 : 3.20 mm
内部方法
%
0
Shrinkage rate
横向流动 2
内部方法
%
0
Shrinkage rate
横向流动 : 3.20 mm
内部方法
%
0
Specific volume
ASTM D792
cm³/g
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE JAPAN/420SE0-1001
Tensile strength
屈服 4
ASTM D638
Mpa
1
Tensile strength
屈服
ISO 527-2/5
Mpa
1
Tensile strength
断裂 4
ASTM D638
Mpa
1
Tensile strength
断裂
ISO 527-2/5
Mpa
1
Tensile modulus
-- 3
ASTM D638
Mpa
1
Tensile modulus
--
ISO 527-2/1
Mpa
1
elongation
屈服 4
ASTM D638
%
2
elongation
屈服
ISO 527-2/5
%
1
elongation
断裂 4
ASTM D638
%
2
elongation
断裂
ISO 527-2/5
%
1
Taber abraser
1000 Cycles, 1000 g, CS-17 转轮
内部方法
mg
2
Bending modulus
50.0 mm 跨距 5
ASTM D790
Mpa
9
Bending modulus
-- 6
ISO 178
Mpa
9
Bending stress
--
ISO 178
Mpa
1
Bending stress
断裂, 50.0 mm 跨距 5
ASTM D790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE JAPAN/420SE0-1001
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
thermal conductivity
ISO 8302
W/m/K
0
Vicat softening temperature
--
ASTM D152510, ISO 306/B50, ISO 306/B120
°C
2
Vicat softening temperature
--
ISO 306/A50
°C
2
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831, ISO 11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
流动 : 23 到 80°C
ISO 11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
8
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
横向 : 23 到 80°C
ISO 11359-2
cm/cm/°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
2
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 9
ISO 75-2/Be
°C
2
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
2
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9
ISO 75-2/Ae
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8
ISO 75-2/Af
°C
2
Electrical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE JAPAN/420SE0-1001
Surface resistivity
IEC 60093
ohms
>
Dielectric strength
1.60 mm, in Oil
ASTM D149
KV/mm
2
Dielectric strength
3.20 mm, in Air
ASTM D149
KV/mm
1
Dielectric strength
0.800 mm, 在油中
IEC 60243-1
KV/mm
2
Dielectric strength
1.60 mm, 在油中
IEC 60243-1
KV/mm
2
Dielectric strength
3.20 mm, 在油中
IEC 60243-1
KV/mm
1
Leakage Trace Index
--
IEC 60112
V
1
Leakage Trace Index
解决方案 B
IEC 60112
V
1
Volume resistivity
ASTM D257, IEC 60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE JAPAN/420SE0-1001
Impact strength of simply supported beam gap 7
-30°C
ISO 179/1eA
kJ/m²
6
Impact strength of simply supported beam gap 7
23°C
ISO 179/1eA
kJ/m²
7
The impact strength of a simply supported beam without a notch is 7
-30°C
ISO 179/1eU
kJ/m²
5
The impact strength of a simply supported beam without a notch is 7
23°C
ISO 179/1eU
kJ/m²
5
Non notched cantilever beam impact
23°C
ASTM D4812
J/m
6
Non notched cantilever beam impact
-30°C 8
ISO 180/1U
kJ/m²
4
Non notched cantilever beam impact
23°C 8
ISO 180/1U
kJ/m²
4
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
5
hardness
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE JAPAN/420SE0-1001
Ball pressure hardness
H 358/30
ISO 2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE JAPAN/420SE0-1001
Extreme Oxygen Index
ISO 4589-2
%
3
Burning wire flammability index
1.0 mm
IEC 60695-2-12
°C
9