Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5101G-30U TORAY JAPAN
Toraycon®
Electrical components、Automotive Applications
High impact resistance、Fast forming cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/5101G-30U
Shrinkage rate
TD:3.00mm2
内部方法
%
1
Shrinkage rate
MD:3.00mm3
内部方法
%
0
Water absorption rate
23°C,24hr
ISO62
%
0
Water absorption rate
23℃,24hr
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/5101G-30U
IZOD notch impact strength
缺口，23℃
ASTM D256
J/m
1
IZOD notch impact strength
无缺口，23℃
ASTM D256
KJ/m
8
Tensile modulus
23°C
ISO527-2
Mpa
8
tensile strength
23℃
ASTM D638
Mpa
1
Tensile strain
断裂,23°C
ISO527-2
%
4
Tensile stress
23°C
ISO527-2
Mpa
1
Rockwell hardness
ASTM D785
M
8
elongation
23℃
ASTM D638
%
5
Bending modulus
23℃
ASTM D790
GPa
7
Bending modulus
23°C
ISO178
Mpa
8
bending strength
23℃
ASTM D790
Mpa
1
Bending stress
23°C
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/5101G-30U
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Hot deformation temperature
-，0.45MPa
ASTM D648
°C
2
Hot deformation temperature
-，1.82Mpa
ASTM D648
°C
2
Linear coefficient of thermal expansion
MD：-30到100°C
ISO11359-2
cm/cm/°C
4
Electrical performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/5101G-30U
Arc resistance coefficient
ASTM D495
S
1
Arc resistance 7
IEC60950
sec
1
Voltage endurance
ASTM D149
MV/m
3
Volume resistivity
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/5101G-30U
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
6
Supplementary Information
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/5101G-30U
BarFlowLength8
250°C,1.00mm
内部方法
CM
6