Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 310SEO-1001 SABIC INNOVATIVE NANSHA
VALOX™
Electrical field、Electronic field、Industrial applications、Switch panel、Shell
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/310SEO-1001
Melt flow rate
250°C/2.16 kg
ASTM D1238
g/10 min
8
Molten Volume Flow Rate (MVR)
250°C/2.16 kg
ISO 1133
cm3/10min
8
Shrinkage rate
横向流动 : 2.30 到 4.60 mm
内部方法
%
1
Shrinkage rate
横向流动 : 0.750 到 2.30 mm
内部方法
%
1
Shrinkage rate
横向流动 2
内部方法
%
0
Shrinkage rate
流动 : 2.30 到 4.60 mm
内部方法
%
1
Shrinkage rate
流动 : 3.20 mm
内部方法
%
1
Shrinkage rate
流动 : 0.750 到 2.30 mm
内部方法
%
0
Shrinkage rate
流动 2
内部方法
%
1
Specific volume
ASTM D792
cm³/g
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/310SEO-1001
Tensile strength
断裂
ISO 527-2/50
Mpa
4
Tensile strength
断裂 4
ASTM D638
Mpa
5
Tensile strength
屈服
ISO 527-2/50
Mpa
5
Tensile strength
屈服 4
ASTM D638
Mpa
5
Tensile modulus
--
ISO 527-2/1
Mpa
2
Tensile modulus
-- 3
ASTM D638
Mpa
2
elongation
断裂
ISO 527-2/50
%
1
elongation
断裂 4
ASTM D638
%
1
elongation
屈服
ISO 527-2/50
%
5
elongation
屈服 4
ASTM D638
%
5
Taber abraser
1000 Cycles, 1000 g, CS-17 转轮
内部方法
mg
1
Bending modulus
50.0 mm 跨距 5
ASTM D790
Mpa
2
Bending modulus
-- 6
ISO 178
Mpa
2
Bending stress
-- 6, 7
ISO 178
Mpa
9
Bending stress
屈服, 50.0 mm 跨距 5
ASTM D790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/310SEO-1001
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
thermal conductivity
ISO 8302
W/m/K
0
Vicat softening temperature
--
ASTM D152511, ISO 306/B50, ISO 306/B120
°C
1
Vicat softening temperature
--
ISO 306/A50
°C
2
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
流动 : 60 到 138°C
ASTM E831
cm/cm/°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
流动 : 23 到 60°C
ISO 11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : 23 到 60°C
ISO 11359-2
cm/cm/°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Thermal deformation temperature under load
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 10
ISO 75-2/Be
°C
1
Thermal deformation temperature under load
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
7
Thermal deformation temperature under load
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
7
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 10
ISO 75-2/Ae
°C
6
Thermal deformation temperature under load
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9
ISO 75-2/Af
°C
7
Electrical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/310SEO-1001
Surface resistivity
IEC 60093
ohms
>
Dielectric strength
1.60 mm, in Oil
ASTM D149
KV/mm
2
Dielectric strength
3.20 mm, in Air
ASTM D149
KV/mm
1
Dielectric strength
0.800 mm, 在油中
IEC 60243-1
KV/mm
3
Dielectric strength
1.00 mm 12
IEC 60243-1
KV/mm
1
Dielectric strength
1.60 mm, 在油中
IEC 60243-1
KV/mm
2
Dielectric strength
3.20 mm, 在油中
IEC 60243-1
KV/mm
1
Leakage Trace Index
--
IEC 60112
V
1
Leakage Trace Index
解决方案 B
IEC 60112
V
1
Volume resistivity
IEC 60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/310SEO-1001
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
2
hardness
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/310SEO-1001
Ball pressure hardness
H 358/30
ISO 2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/310SEO-1001
Extreme Oxygen Index
ISO 4589-2
%
3
Burning wire flammability index
1.0 mm
IEC 60695-2-12
°C
9