Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC LUX9612G-WH8A508X SABIC INNOVATIVE NANSHA
LEXAN™
Electronic display、Lighting applications
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9612G-WH8A508X
Melt volume flow rate
300°C/1.2kg
ISO1133
cm3/10min
7
Melt mass flow rate
300°C/1.2kg
ASTMD1238
g/10min
7
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
MD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,100°C
ASTMD570
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9612G-WH8A508X
Tensile strength 3
屈服
ASTMD638
Mpa
6
Tensile strength 3
断裂
ASTMD638
Mpa
6
Tensile modulus
ISO527-2/1
Mpa
2
Tensile modulus
ISO527-2/1
Mpa
2
Tensile modulus 2
ASTMD638
Mpa
2
Tensile strain
断裂
ISO527-2/50
%
7
Tensile strain
屈服
ISO527-2/50
%
6
Tensile strain
断裂
ISO527-2/50
%
1
Tensile stress
屈服
ISO527-2/50
Mpa
6
Tensile stress
断裂
ISO527-2/50
Mpa
6
Tensile stress
断裂
ISO527-2/50
Mpa
5
Tensile stress
屈服
ISO527-2/50
Mpa
6
Elongation rate 3
屈服
ASTMD638
%
6
Elongation rate 4
断裂
ASTMD638
%
8
Bending modulus 2
ISO178
Mpa
2
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus 5
ISO178
Mpa
2
Bending strength 4
屈服,50.0mm跨距
ASTMD790
Mpa
9
Bending strength 6,7
ISO178
Mpa
9
Bending stress 2,3
ISO178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9612G-WH8A508X
RTI
UL746
°C
1
RTIElec
UL746
°C
1
Evolution Calendar intelligent importer
UL746
°C
1
RTIStr
UL746
°C
1
specific heat
ASTMC351
J/kg/°C
1
thermal conductivity
ASTMC177
W/m/K
0
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
1
Hot deformation temperature 6
0.45MPa,未退火,64.0mm跨距
ISO75-2/Bf
°C
1
Hot deformation temperature 6
1.8MPa,未退火,64.0mm跨距
ISO75-2/Af
°C
1
Hot deformation temperature 9
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
1
Hot deformation temperature 9
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
1
Vicat softening temperature
ASTMD152510
°C
1
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Linear coefficient of thermal expansion
MD:-40到40°C
ASTME831
cm/cm/°C
6
Linear coefficient of thermal expansion
TD:-40到40°C
ASTME831
cm/cm/°C
6
Electrical performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9612G-WH8A508X
Dielectric strength
3.20mm,inAir
ASTMD149
KV/mm
1
Volume resistivity
IEC60093
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9612G-WH8A508X
NotchedIzodImpactStrength8
23°C
ISO180/1A
kJ/m²
4
Multi axis Instrumented Impact Energy
ISO6603-2
J
1
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
7
flammability
Test Condition
Test Method
Unit
PC/SABIC INNOVATIVE NANSHA/LUX9612G-WH8A508X
Hot filament ignition temperature
1.0mm
IEC60695-2-13
°C
8
Hot filament ignition temperature
1.5mm
IEC60695-2-13
°C
8
Burning wire flammability index
0.8mm
IEC60695-2-12
°C
7
Burning wire flammability index
1.0mm
IEC60695-2-12
°C
9
Burning wire flammability index
1.5mm
IEC60695-2-12
°C
8