Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS 6565A6 JAPAN POLYPLASTIC
DURAFIDE®
Electrical field、Electronic field
transparent、High temperature resistan、High mobility、Flame retardant、Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/6565A6
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/6565A6
Melt viscosity
310°C,1000sec^-1
ISO11443
mPa·s
2
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/6565A6
elongation at break
ASTM D638/ISO 527
%
1
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
Tensile strain
断裂
ISO527-2
%
1
Tensile stress
ISO527-2
Mpa
1
Bending modulus
ISO178
Mpa
1
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
Bending stress
ISO178
Mpa
1
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
4
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
1
Thermal performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/6565A6
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
vicat softening point
ASTM D1525/ISO R306
℃（℉）
2
Linear coefficient of thermal expansion
MD
内部方法
cm/cm/°C
1
Linear coefficient of thermal expansion
TD
内部方法
cm/cm/°C
3
Electrical performance
Test Condition
Test Method
Unit
PPS/JAPAN POLYPLASTIC/6565A6
Dissipation factor
耐电弧性
IEC60250
sec
1
Dielectric strength
3.00mm
IEC60243-1
KV/mm
1
Leakage Trace Index
IEC60112
V
2
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
2
Volume resistivity
IEC60093
ohms·cm
2