density

23°C

ISO 1183

g/cm³

1

Shrinkage rate 2

横向流量 : 3.00 mm

内部方法

%

0

Shrinkage rate 2

流量 : 3.00 mm

内部方法

%

0

Water absorption rate

24 hr, 23°C

ISO 62

%

0

Water absorption rate

饱和, 23°C

ISO 62

%

4

shear strength

23°C

ASTM D732

Mpa

1

Tensile strain

断裂, -40°C

ISO 527-2

%

2

Tensile strain

断裂, 23°C

ISO 527-2

%

3

Tensile strain

断裂, 80°C

ISO 527-2

%

5

Tensile stress

-40°C

ISO 527-2

Mpa

2

Tensile stress

23°C

ISO 527-2

Mpa

2

Tensile stress

80°C

ISO 527-2

Mpa

1

Bending modulus

-40°C

ISO 178

Mpa

1

Bending modulus

23°C

ISO 178

Mpa

1

Bending modulus

80°C

ISO 178

Mpa

8

Bending stress

-40°C

ISO 178

Mpa

3

Bending stress

23°C

ISO 178

Mpa

3

Bending stress

80°C

ISO 178

Mpa

2

Compressive stress

-40°C

ISO 604

Mpa

2

Compressive stress

23°C

ISO 604

Mpa

1

Compressive stress

80°C

ISO 604

Mpa

1

Hot deformation temperature

0.45 MPa, 未退火

ISO 75-2/B

°C

2

Melting temperature

DSC

°C

2

Linear coefficient of thermal expansion - flow

ISO 11359-2

cm/cm/°C

2

Dielectric strength

IEC 60243-1

KV/mm

1

Volume resistivity

IEC 60093

ohms·cm

1

Charpy Notched Impact Strength

-40°C

ISO 179

kJ/m²

1

Charpy Notched Impact Strength

23°C

ISO 179

kJ/m²

1

Impact strength of simply supported beam without notch

-40°C

ISO 179

kJ/m²

8

Impact strength of simply supported beam without notch

23°C

ISO 179

kJ/m²

9