Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 GF40-02 CELANESE USA
CELSTRAN®
Electrical components、Electronic and electrical
enhance、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Mechanical performance
Test Condition
Test Method
Unit
PA66/CELANESE USA/GF40-02
elongation at break
23℃
ISO75-2
%
2
elongation at break
80℃
ISO75-2
%
2
Charpy impact strength
23℃
ISO 179 1eU
KJ/m
9
Charpy Notched Impact Strength
23℃
ISO 179 1eA
KJ/m
3
Charpy Notched Impact Strength
-30℃
ISO 179 1eA
KJ/m
3
Tensile modulus
23℃
ISO 527,part 1/2,1mm/min
Mpa
1
Tensile modulus
80℃
ISO 527,part 1/2,1mm/min
Mpa
7
tensile strength
23℃
ISO75-2
Mpa
1
tensile strength
80℃
ISO75-2
Mpa
1
Bending modulus
23℃
ISO 178
Mpa
9
Bending modulus
80℃
ISO 178
Mpa
6
bending strength
23℃
ISO 178
Mpa
2
bending strength
80℃
ISO 178
Mpa
2
Corresponding bending strain under bending strength
23℃
ISO 178
%
4
Corresponding bending strain under bending strength
80℃
ISO 178
%
3
Impact strength of cantilever beam gap
23℃
ASTM D-256
J/m
2
Thermal performance
Test Condition
Test Method
Unit
PA66/CELANESE USA/GF40-02
Hot deformation temperature
HDT/A(1.8MPa)
ISO 75 part 1/2
°C
2
Hot deformation temperature
HDT/B(8.0MPa)
ISO 75 part 1/2
°C
2
Basic performance
Test Condition
Test Method
Unit
PA66/CELANESE USA/GF40-02
density
ISO 1183
g/cm
1
Water absorption rate
24h 23℃
ISO 62
% by wt.
0
Enhance material content
ISO 3451,part 1
% by wt.
4