Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 6300B JAPAN POLYPLASTIC
DURANEX®
Automotive Applications
Low warpage
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/6300B
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/6300B
Tensile failure strain
ISO 527-1/-2
%
2
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
5
tensile strength
ISO 527-1/-2
Mpa
5
Tensile strain
断裂
ISO527-2
%
5
Tensile stress
ISO527-2
Mpa
5
Bending modulus
ISO 178
Mpa
3
Bending modulus
ISO178
Mpa
3
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
3
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
9
bending strength
ISO 178
Mpa
9
Bending stress
ISO178
Mpa
9
Charpy notch impact strength
ISO 179/1eA
kJ/m²
2
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
2
Thermal performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/6300B
Hot deformation temperature
1.8Mpa
ISO 75-1/-2
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
1
Coefficient of linear expansion
-，流动方向
ISO 11359-2
×10-5/℃
9
Coefficient of linear expansion
-，垂直方向
ISO 11359-2
×10-5/℃
9
Linear coefficient of thermal expansion
MD：23到55°C
内部方法
cm/cm/°C
9
Linear coefficient of thermal expansion
TD：23to55°C
内部方法
cm/cm/°C
9
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
9
Electrical performance
Test Condition
Test Method
Unit
PBT/JAPAN POLYPLASTIC/6300B
Surface resistivity
IEC 60093
Ω
5
Dielectric strength
3.00mm
IEC60243-1
KV/mm
2
Leakage Trace Index
IEC60112
V
3
Volume resistivity
IEC60093
ohms·cm
8
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
8
Volume resistivity
IEC 60093
Ω.cm
8