Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PET X8300 SABIC INNOVATIVE US
XYLEX™
Electrical field、Electronic field
UV resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/PET/SABIC INNOVATIVE US/X8300
Density/specific gravity
ASTMD792
g/cm³
1
Density/specific gravity
ISO1183
g/cm³
1
Melt volume flow rate
265°C/2.16kg
ISO1133
cm3/10min
1
Melt mass flow rate
265°C/2.16kg
ASTMD1238
g/10min
1
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD：3.20mm
内部方法
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/PET/SABIC INNOVATIVE US/X8300
Tensile strength 3
断裂
ASTMD638
Mpa
4
Tensile strength 3
屈服
ASTMD638
Mpa
4
Tensile modulus
ISO527-2/1
Mpa
1
Tensile modulus 2
ASTMD638
Mpa
1
Tensile strain
屈服
ISO527-2/50
%
>
Tensile strain
断裂
ISO527-2/50
%
>
Tensile stress
屈服
ISO527-2/50
Mpa
5
Tensile stress
断裂
ISO527-2/50
Mpa
5
Elongation rate 3
屈服
ASTMD638
%
5
Elongation rate 4
断裂
ASTMD638
%
1
Bending modulus 4
50.0mm跨距
ASTMD790
Mpa
1
Bending modulus 5
ISO178
Mpa
1
Bending strength 4
屈服,50.0mm跨距
ASTMD790
Mpa
7
Bending strength 5,6
ISO178
Mpa
7
Thermal performance
Test Condition
Test Method
Unit
PC/PET/SABIC INNOVATIVE US/X8300
thermal conductivity
ISO8302
W/m/K
0
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
7
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
7
Hot deformation temperature
1.8MPa,未退火,100mm跨距9
ISO75-2/Ae
°C
8
Hot deformation temperature
1.8MPa,未退火,64.0mm跨距10
ISO75-2/Af
°C
7
Vicat softening temperature
ASTMD152511
°C
9
Vicat softening temperature
ISO306/B120
°C
9
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
1
Linear coefficient of thermal expansion
MD：-40to40°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
MD：23to60°C
ISO11359-2
cm/cm/°C
9
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：-40to40°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：23to60°C
ISO11359-2
cm/cm/°C
9
Electrical performance
Test Condition
Test Method
Unit
PC/PET/SABIC INNOVATIVE US/X8300
Surface resistivity
ASTMD257
ohms
>
Volume resistivity
ASTMD257
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PC/PET/SABIC INNOVATIVE US/X8300
Impact strength of simply supported beam gap 7
23°C
ISO179/1eA
kJ/m²
1
Impact strength of cantilever beam gap
-30°C
ASTMD256
J/m
7
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
1
Suspended wall beam gap impact strength 8
-30°C
ISO180/1A
kJ/m²
7
Suspended wall beam gap impact strength 8
-10°C
ISO180/1A
kJ/m²
5
Suspended wall beam gap impact strength 8
23°C
ISO180/1A
kJ/m²
8
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
9
flammability
Test Condition
Test Method
Unit
PC/PET/SABIC INNOVATIVE US/X8300
Burning wire flammability index
1.0mm
IEC60695-2-12
°C
7
optical performance
Test Condition
Test Method
Unit
PC/PET/SABIC INNOVATIVE US/X8300
transmissivity
2540µm
ASTMD1003
%
8
Haze
2540µm
ASTMD1003
%
1