Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6/6T KR4340G6 BASF GERMANY
Ultramid®
Electronic and Electrical、Automotive components
Low water absorption、Rigidity and strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA6/6T/BASF GERMANY/KR4340G6
Molten Volume Flow Rate (MVR)
325°C/5.0 kg
ISO 1133
cm3/10min
4
Shrinkage rate
横向流量
ISO 294-4
%
0
Shrinkage rate
流量
ISO 294-4
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
4
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
1
Stickiness number
96% H2SO4
ISO 307
cm³/g
1
Mechanical performance
Test Condition
Test Method
Unit
PA6/6T/BASF GERMANY/KR4340G6
Tensile modulus
ISO 527-2
Mpa
1
Tensile strain
断裂
ISO 527-2
%
2
Tensile stress
断裂
ISO 527-2
Mpa
1
Bending modulus
ISO 178
Mpa
1
Bending stress
ISO 178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA6/6T/BASF GERMANY/KR4340G6
Hot deformation temperature
1.8 MPa, 未退火
ISO 75-2/A
°C
2
Melting temperature
ISO 11357-3
°C
2
Electrical performance
Test Condition
Test Method
Unit
PA6/6T/BASF GERMANY/KR4340G6
Surface resistivity
IEC 60093
ohms
-
Leakage Trace Index
解决方案 A
IEC 60112
V
6
Volume resistivity
IEC 60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PA6/6T/BASF GERMANY/KR4340G6
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
kJ/m²
6
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
kJ/m²
6
flammability
Test Condition
Test Method
Unit
PA6/6T/BASF GERMANY/KR4340G6
Extreme Oxygen Index
ISO 4589-2
%
5
Hot filament ignition temperature
0.40 mm
IEC 60695-2-13
°C
7
Burning wire flammability index
0.40 mm
IEC 60695-2-12
°C
9