Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS NH-1015V K21111 LOTTE KOREA
INFINO®
Laptop
enhance、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/LOTTE KOREA/NH-1015V K21111
Melt mass flow rate
220°C/10.0kg
ASTMD1238
g/10min
3
Melt mass flow rate
220°C/10.0kg
ISO1133
g/10min
3
Shrinkage rate
MD：3.20mm
ASTMD955
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/LOTTE KOREA/NH-1015V K21111
Tensile strength 2
屈服
ASTMD638
Mpa
6
Tensile modulus
ISO527-2/50
Mpa
2
Tensile strain
断裂
ISO527-2/50
%
4
Tensile stress
屈服
ISO527-2/50
Mpa
6
Tensile stress
断裂
ISO527-2/50
Mpa
4
Bending modulus 3
ASTMD790
Mpa
2
Bending modulus 4
ISO178
Mpa
2
Bending strength 3
ASTMD790
Mpa
8
Bending stress 4
ISO178
Mpa
8
Thermal performance
Test Condition
Test Method
Unit
PC/ABS/LOTTE KOREA/NH-1015V K21111
RTIElec
1.5mm
UL746
°C
9
Evolution Calendar intelligent importer
1.5mm
UL746
°C
8
RTIStr
1.5mm
UL746
°C
9
Hot deformation temperature
0.45MPa,Unannealed,4.00mm
ISO75-2/B
°C
9
Hot deformation temperature
0.45MPa,Annealed,4.00mm
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火,6.40mm
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,Unannealed,4.00mm
ISO75-2/A
°C
8
Hot deformation temperature
1.8MPa,Annealed,4.00mm
ISO75-2/A
°C
9
Vicat softening temperature
--
ISO306/B50
°C
1
Vicat softening temperature
--
ISO306/B120
°C
1
Impact performance
Test Condition
Test Method
Unit
PC/ABS/LOTTE KOREA/NH-1015V K21111
CharpyNotchedImpactStrength5
23°C
ISO179/1eA
kJ/m²
1
Suspended wall beam gap impact strength 5
23°C
ISO180/1A
kJ/m²
1