Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ASA XP4034 SABIC INNOVATIVE US
GELOY™
Automotive sector
High mobility、Thermal stability、Antistatic、Weather resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ASA/SABIC INNOVATIVE US/XP4034
Melt mass flow rate
220°C/10.0 kg
ASTM D1238
g/10 min
5
Melt mass flow rate
260°C/5.0 kg
ASTM D1238
g/10 min
1
Melt mass flow rate
280°C/3.8 kg
ASTM D1238
g/10 min
2
Shrinkage rate
流动 : 3.20 mm
内部方法
%
0
Shrinkage rate
横向流动 : 3.20 mm
内部方法
%
0
Water absorption rate
24 hr
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
ASA/SABIC INNOVATIVE US/XP4034
Tensile modulus
ISO 527-2/1
Mpa
2
tensile strength
屈服 2
ASTM D638
Mpa
6
tensile strength
屈服
ISO 527-2/50
Mpa
5
tensile strength
断裂
ISO 527-2/50
Mpa
5
elongation
屈服
ISO 527-2/50
%
4
elongation
断裂 2
ASTM D638
%
2
elongation
断裂
ISO 527-2/50
%
1
Bending modulus
50.0 mm 跨距 3
ASTM D790
Mpa
2
Bending modulus
-- 4
ISO 178
Mpa
2
bending strength
-- 4, 5
ISO 178
Mpa
7
bending strength
屈服, 50.0 mm 跨距 3
ASTM D790
Mpa
8
Dart impact equipped with measuring instruments
-30°C, Total Energy
ASTM D3763
J
3
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
4
Thermal performance
Test Condition
Test Method
Unit
ASA/SABIC INNOVATIVE US/XP4034
thermal conductivity
ASTM C177
W/m/K
0
Hot deformation temperature
0.45 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Hot deformation temperature
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7
ISO 75-2/Bf
°C
1
Hot deformation temperature
1.8 MPa, 未退火, 6.40 mm
ASTM D648
°C
1
Hot deformation temperature
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 7
ISO 75-2/Af
°C
9
vicat softening point
ISO 306/B50
°C
1
Linear coefficient of thermal expansion
流动 : -20 到 150°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -20 到 150°C
ASTM E831
cm/cm/°C
7