Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEEK 330G JILIN JOINATURE
ZYPEEK®
Aerospace、Automotive sector
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PEEK/JILIN JOINATURE/330G
Density
结晶
ISO 1183
g/cm³
1
Density
非结晶
ISO 1183
g/cm³
1
Melt mass flow rate
380℃，5.0kg
ISO 1133
g/10min
8
Shrinkage rate
MD
ISO 294-4
%
1
Shrinkage rate
TD
ISO 294-4
%
1
Water absorption rate
23℃，24hr，3.2 mm厚拉伸棒
ISO 62-1
%
0
Water absorption rate
平衡，23℃
ISO 62-1
%
0
Mechanical performance
Test Condition
Test Method
Unit
PEEK/JILIN JOINATURE/330G
Tensile strength
屈服，23℃
ISO 527
Mpa
1
Tensile strain
断裂，23℃
ISO 527
%
2
Shore hardness
23℃
ISO 868
D 级
8
Bending modulus
23℃
ISO 178
Mpa
4
Bending strength
屈服，23℃
ISO 178
Mpa
1
Compressive strength
23℃
ISO 604
Mpa
1
Impact performance
Test Condition
Test Method
Unit
PEEK/JILIN JOINATURE/330G
Impact strength of simply supported beam gap
ISO 179-1eA
kJ/m²
4
Impact strength of simply supported beam without notch
ISO 179/1U
kJ/m²
-
Impact strength of cantilever beam gap
ISO 180/A
kJ/m²
5
Cantilever beam without notch impact strength
ISO 180/U
kJ/m²
-
Thermal performance
Test Condition
Test Method
Unit
PEEK/JILIN JOINATURE/330G
Specific heat capacity
23℃
DSC
kJ/kg /℃
2
Hot deformation temperature
1.8 Mpa
ISO 75-f
°C
1
Thermal conductivity coefficient
23℃
ISO 22007-4
W/m/K
0
Melting point
Tg（起始）
ISO 11357
°C
1
Linear coefficient of thermal expansion
低于Tg沿着流动方向
ISO 11359
ppm/K
5
Linear coefficient of thermal expansion
高于Tg沿着流动方向
ISO 11359
ppm/K
1
Electrical performance
Test Condition
Test Method
Unit
PEEK/JILIN JOINATURE/330G
Dielectric strength
2 mm
IEC 60243-1
KV/mm
2
Volume resistivity
275 ℃
IEC 60093
ohms·cm
1
Volume resistivity
23 ℃，1V
IEC 60093
ohms·cm
1
Compared to the leakage trace index
IEC 60112
V
1