Melt flow rate

300°C/1.2 kg

ASTM D1238

g/10 min

2

Molten Volume Flow Rate (MVR)

300°C/1.2 kg

ISO 1133

cm3/10min

2

Shrinkage rate - flow

-- 2

内部方法

%

0

Shrinkage rate - flow

3.20 mm

内部方法

%

0

Water absorption rate

饱和, 23°C

ISO 62

%

0

Water absorption rate

平衡, 23°C

ASTM D570

%

0

Tensile strength

屈服 4

ASTM D638

Mpa

6

Tensile strength

屈服

ISO 527-2/50

Mpa

6

Tensile modulus

-- 3

ASTM D638

Mpa

2

Tensile modulus

--

ISO 527-2/1

Mpa

2

elongation

屈服 4

ASTM D638

%

6

elongation

屈服

ISO 527-2/50

%

6

elongation

断裂 4

ASTM D638

%

>

elongation

断裂

ISO 527-2/50

%

>

Bending modulus

50.0 mm 跨距 5

ASTM D790

Mpa

2

Bending modulus

-- 6

ISO 178

Mpa

2

Bending stress

-- 6, 7

ISO 178

Mpa

9

Bending stress

屈服, 50.0 mm 跨距 5

ASTM D790

Mpa

9

thermal conductivity

ASTM C177, ISO 8302

W/m/K

0

Vicat softening temperature

ISO 306/B50, ASTM D152510

°C

1

Linear coefficient of thermal expansion - flow

-40 到 95°C

ASTM E831

cm/cm/°C

7

Linear coefficient of thermal expansion - flow

23 到 80°C

ISO 11359-2

cm/cm/°C

7

Thermal deformation temperature under load

0.45 MPa, 未退火, 3.20 mm

ASTM D648

°C

1

Thermal deformation temperature under load

0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9

ISO 75-2/Bf

°C

1

Thermal deformation temperature under load

1.8 MPa, 未退火, 3.20 mm

ASTM D648

°C

1

Thermal deformation temperature under load

1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9

ISO 75-2/Af

°C

1

Dielectric strength

1.60 mm

ASTM D149, IEC 60243-1

KV/mm

2

Volume resistivity

ASTM D257, IEC 60093

ohms·cm

>

Dart impact equipped with measuring instruments

23°C, Energy at Peak

ASTM D3763

J

5

transmissivity

2540 µm

ASTM D1003

%

8

Haze

2540 µm

ASTM D1003

%

<