Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 CM1017XL3 TORAY JAPAN
Amilan®
Electrical components、Electrical appliances、Automotive sector、Shell
heat-resisting、Low temperature toughness、Fast forming cycle
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1017XL3
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
1
physical property
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1017XL3
Shrinkage rate
MD：1.00mm3
%
--
0
Shrinkage rate
MD：3.00mm4
%
--
1
Water absorption rate
23°C,24hr
%
--
1
Water absorption rate
饱和,23°C
%
--
1
Mechanical performance
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1017XL3
shear strength
23°C
MPa
65.0
7
Tensile strain
屈服,23°C
%
--
1
Tensile stress
23°C
MPa
35.0
8
Tensile stress
80°C
MPa
20.0
2
Taber abraser
1000Cycles
mg
--
3
Bending modulus
-40°C
MPa
3600
3
Bending modulus
80°C
MPa
300
7
Bending stress
23°C
MPa
40.0
1
Bending stress
80°C
MPa
25.0
4
Compressive stress
23°C
MPa
--
8
Thermal performance
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1017XL3
specific heat
J/kg/°C
--
1
thermal conductivity
W/m/K
--
0
Hot deformation temperature
0.45MPa,未退火
°C
--
1
Melting temperature
°C
--
2
Linear coefficient of thermal expansion
MD
cm/cm/°C
--
8
Electrical performance
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1017XL3
Dielectric strength
kV/mm
--
2
Arc resistance 7
sec
--
1
Volume resistivity
ohms·cm
1.0E+11到1.0E+12
1
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
1
Compared to the anti leakage trace index
CTI
V
--
6