ABS Terlux® 2822HD BASF GERMANY

157

Unit Price:
$7041 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
16MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate		ISO294-4	0.40to0.70	%
Water absorption rate	Saturation,23°C	ISO62	0.70	%
Apparent density			0.59	g/cm³
Melt volume flow rate	220°C/10.0kg	ISO1133	2.00	cm3/10min
Melt volume flow rate	Melt volume flow rate	220°C/21.6kg	ISO1133	17.0	cm3/10min

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Yield,23°C	ISO527-2	48.0	Mpa
Tensile strain	Yield,23°C	ISO527-2	4.0	%
Bending stress		ISO178	70.0	Mpa
Nominal tensile fracture strain	23°C	ISO527-2	12	%
Tensile creep modulus	1000hr	ISO899-1	1250	Mpa
Tensile modulus		ISO527-2	2000	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Vicat softening temperature	--	ISO306/B50	93.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO306/A50	105	°C
thermal conductivity		DIN52612	0.17	W/m/K
Hot deformation temperature 3	0.45MPa,Annealed	ISO75-2/B	94.0	°C
Hot deformation temperature 3	Hot deformation temperature 3	1.8MPa,Annealed	ISO75-2/A	90.0	°C
Linear coefficient of thermal expansion	MD	ISO11359-2	8.0E-5to1.1E-4	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	1E+15	ohms
Dielectric constant	100Hz	IEC60250	2.90
Volume resistivity		IEC60093	1E+15	ohms·cm
Dissipation factor	100Hz	IEC60250	0.016
Dissipation factor	Dissipation factor	1MHz	IEC60250	0.014

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179	80	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179	120	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness		ISO2039-1	70.0	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
Refractive index		ISO489	1.540

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.