PPS Susteel® GS-40 TOSOH JAPAN

Unit Price:
$4107 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Method	Test Result	Unit
Density	ASTM D792/ISO 1183	1.64
Modeling Shrinkage	ASTM D955	0.3~0.8	%
Moisture Absorption 23℃/24H	ASTM D570/ISO 62	0.02	%

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD	ISO294-4	0.80	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	0.30	%
Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	<0.020	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Stress	Yield	ISO527-2	176	Mpa
Tensile Strain	Break	ISO527-2	1.5	%
Charpy impact strength	有Notched	ASTM D-256	74	J/m
Charpy impact strength	Charpy impact strength	Unnotched	ASTM D-256	541	J/m
Flexural Stress		ISO178	275	Mpa
Tensile Elongation		ASTM D-638	1.7	%
Tensile Elongation?(Break)		ASTM D638/ISO 527	1.5	%
Tensile Strength		ASTM D638/ISO 527	176	kg/cm²(MPa)[Lb/in²]
Tensile Strength	Tensile Strength		ASTM D-638	172	Mpa
Rockwell Hardness		ASTM D-785	122
Flexural Modulus		ASTM D790/ISO 178	14700	kg/cm²(MPa)[Lb/in²]
	Flexural Modulus		ASTM D-790	15	GPa
	Flexural Modulus	Flexural Modulus		ISO178	14700	Mpa
Flexural Strength		ASTM D790/ISO 178	275	kg/cm²(MPa)[Lb/in²]
Flexural Strength	Flexural Strength		ASTM D-790	275	Mpa
TensileWeldStrength		内部方法	60.0	Mpa
Izod notch impact strength		ASTM D256/ISO 179	82	kg·cm/cm(J/M)ft·lb/in

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Melting temperature		内部方法	285	°C
Deflection Temperature Under Load?	1.82MPa	ASTM D-648	＞260	°C
	Deflection Temperature Under Load?		ASTM D648/ISO 75	260	℃（℉）
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	>260	°C
Melting Temperature			285	℃（℉）
Coefficient of Linear Thermal Expansion		自定标准	2.2
Flame retardancy		UL 94	V-0

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	1MHz	IEC60250	1.4E-03
Comparative Tracking Index	CTI	UL746	PLC4
Dielectric Strength		IEC60243-1	16	KV/mm
Dielectric Constant	1MHz	IEC60250	3.90
	Dielectric Constant	1MHz	ASTM D-150	3.9
	Dielectric Constant	Dielectric Constant		ASTM D150/IEC 60250	3.90
Volume Resistivity		IEC60093	1E+17	ohms·cm
Volume Resistivity		ASTM D-257	4×1016	Ω.cm
Dissipation Factor	1MHz	ASTM D-150	0.0014
Dielectric Strength		ASTM D-149	16	KV/mm
Thermal Conductivity		自定标准	0.27	W/m.K
Comparative Tracking Index		IEC60112	125	V

Processing	Test Condition	Test Method	Test Result	Unit
Drying conditions			120~150度 2.0～5.0hr
Screw Speed			100~150	rpm
Pressure			1.00~20.0	Mpa
Modeling Shrinkage	Flow	ASTM D-955	0.3	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow	ASTM D-955	0.7	%
Mold Temperature			135~150	°C
Processing temperature			270~300	°C
Processing temperature	Processing temperature			290~330	°C

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating		UL94	V-0

Supplementary information	Test Condition	Test Method	Test Result	Unit
BarFlowLength		内部方法	175	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.