Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Flow | 东丽法 | 0.15 | % |
Modeling Shrinkage | 垂重方向 | 东丽法 | 0.55 | % |
Spiral Flow | 320℃,98MPa,1mm厚 | 东丽法 | 90 | |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Taber Abrasion Resistance | | ASTM D-1044 | 70 | mg/1000回 |
Tensile Strength(Break) | | ASTM D-732 | 60 | |
Tensile strength | | ASTM D-638 | 140 | Mpa |
Coefficient of Friction | 对钢 | ASTM D-1894 | 0.30 | |
PV | | 东丽法 | 815 | KJ/m |
Flexural Strength | | ASTM D-790 | 17.6 | GPa |
Impact Strength | Notched23℃ | ASTM D-256 | 90 | J/m |
Impact Strength | Unnotched23℃ | ASTM D-256 | 20 | KJ/m |
hardness | | ASTM D-785 | 123 | 洛氏 |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 0.9 | % |
Tensile Strength | | ASTM D638/ISO 527 | 141(MPa) | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | | ASTM D-638 | 1.2 | % |
Rockwell Hardness | | ASTM D785 | 123 | |
Flexural Strength | | ASTM D790/ISO 178 | 240(MPa) | kg/cm²(MPa)[Lb/in²] |
Flexural Strength | | ASTM D-790 | 200 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | UL94 | V-0 | |
Deflection Temperature Under Load? | 1.82MPa | ASTM D-648 | >260 | °C |
Melting Temperature | | | 278 | ℃(℉) |
Melting Temperature | | DSC | 278 | °C |
Flammability | | UL-94 | V-0 | |
Coefficient of Linear Thermal Expansion | Flow | ASTM D-696 | 1.6 | |
Coefficient of Linear Thermal Expansion | 垂重方向 | ASTM D-696 | 2.4 | |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Arc Resistance | | ASTM D-495 | 182 | 秒 |
Dielectric Constant | 10 | ASTM D-150 | 0.002 | |
Volume Resistivity | | ASTM D-257 | 10 | Ω.m |
Insulation Resistance | | ASTM D-149 | 15 | MV/m |
Dissipation Factor | 10 | ASTM D-150 | 5.8 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | | ASTM D-570 | 0.02 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.