Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Flow | 东丽法 | 0.15 | % |
| Modeling Shrinkage | 垂重方向 | 东丽法 | 0.55 | % |
| Spiral Flow | 320℃,98MPa,1mm厚 | 东丽法 | 90 | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Taber Abrasion Resistance | | ASTM D-1044 | 70 | mg/1000回 |
| Impact Strength | Notched23℃ | ASTM D-256 | 90 | J/m |
| Impact Strength | Unnotched23℃ | ASTM D-256 | 20 | KJ/m |
| Tensile Strength | | ASTM D-638 | 1.2 | % |
| Flexural Strength | | ASTM D-790 | 200 | Mpa |
| hardness | | ASTM D-785 | 123 | 洛氏 |
| Tensile Strength(Break) | | ASTM D-732 | 60 | |
| Tensile strength | | ASTM D-638 | 140 | Mpa |
| Coefficient of Friction | 对钢 | ASTM D-1894 | 0.30 | |
| PV | | 东丽法 | 815 | KJ/m |
| Flexural Strength | | ASTM D-790 | 17.6 | GPa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melting Temperature | | DSC | 278 | °C |
| Deflection Temperature Under Load? | 1.82MPa | ASTM D-648 | >260 | °C |
| Flammability | | UL-94 | V-0 | |
| Coefficient of Linear Thermal Expansion | Flow | ASTM D-696 | 1.6 | |
| Coefficient of Linear Thermal Expansion | 垂重方向 | ASTM D-696 | 2.4 | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor | 10 | ASTM D-150 | 5.8 | |
| Arc Resistance | | ASTM D-495 | 182 | 秒 |
| Dielectric Constant | 10 | ASTM D-150 | 0.002 | |
| Volume Resistivity | | ASTM D-257 | 10 | Ω.m |
| Insulation Resistance | | ASTM D-149 | 15 | MV/m |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | | ASTM D-570 | 0.02 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.