Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.73 | |
Modeling Shrinkage | | ASTM D955 | 0.2 | % |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.02 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:3.00mm2 | 内部方法 | 0.80 | % |
Modeling Shrinkage | MD:3.00mm4 | 内部方法 | 0.20 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.020 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield,23°C | ISO527-2 | 165 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 1.4 | % |
Flexural Stress | 23°C | ISO178 | 250 | Mpa |
Taber Abrasion Resistance | 1000Cycles | ISO9352 | 50.0 | mg |
Shearing Strength | 23°C | JISK7214 | 75.0 | Mpa |
Coefficient of Friction | | | 0.25 | |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 1.4 | % |
Tensile Strength | | ASTM D638/ISO 527 | 185 | kg/cm²(MPa)[Lb/in²] |
Rockwell Hardness | | ASTM D785 | 123 | |
Flexural Modulus | | ASTM D790/ISO 178 | 15.5 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | 23°C | ISO178 | 15500 | Mpa |
Flexural Strength | | ASTM D790/ISO 178 | 250 | kg/cm²(MPa)[Lb/in²] |
Charpy impact strength | | ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in |
Charpy impact strength | | ASTM D256/ISO 179 | 30 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | UL94 | V-0 | |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | >260 | ℃(℉) |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 260 | °C |
Melting Temperature | | | 278 | ℃(℉) |
Linear expansion coefficient | | ASTM D696/ISO 11359 | 1.9 | mm/mm.℃ |
Linear thermal expansion coefficient | MD | ISO11359-2 | 2.3E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 3.1E-05 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 278 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | IEC60243-1 | 22 | KV/mm |
Dielectric Constant | 23°C,1MHz | IEC60250 | 3.60 | |
Dissipation Factor | 23°C,1MHz | IEC60250 | 2E-03 | |
Dielectric Constant | | ASTM D150/IEC 60250 | 3.6 | |
Volume Resistivity | | ASTM D257/IEC 60093 | 1014 | Ω.cm |
Volume Resistivity | | IEC60093 | 1E+16 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179 | 30 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ISO2039-2 | 123 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.28mm | UL94 | V-0 | |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
BarFlowLength6 | 320°C,1.00mm | 内部方法 | 200 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.