PPS DIC.PPS FZ-1140-D5 DIC JAPAN

219

Unit Price:
$3283 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
103.5MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan Glass fiber reinforced enhance Flame retardant Filler: Glass fiber reinf 40% filler by weight
Application Areas:Fiber grade
Color:--
Grade:Injection grade

Technical Data Sheet

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.66
Water absorption rate 23 ℃/24h		ASTM D570/ISO 62	0.02	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD	ASTMD955	0.25	%
Shrinkage rate	Shrinkage rate	TD	ASTMD955	1.1	%
Water absorption rate	23°C,24hr	ASTMD570	0.020	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Elongation rate		ASTM D-638	1.8	%
compressive strength		ASTMD695	200	Mpa
Friction coefficient 3	Steel - Dynamic	ASTMD1894	0.35
Friction coefficient 3	Friction coefficient 3	Steel - Static	ASTMD1894	0.35
Poisson's ratio			0.36
Tensile strength		ASTMD638	190	Mpa
Fracture bending elongation		ASTMD790	2.5	%
elongation at break		ASTM D638/ISO 527	1.8	%
Tensile modulus		ASTM D638/ISO 527	15000	kg/cm²(MPa)[Lb/in²]
	Tensile modulus		ASTM D-638	15000	Mpa
	Tensile modulus	Tensile modulus		ASTMD638	15000	Mpa
tensile strength		ASTM D-638	175	Mpa
tensile strength	tensile strength		ASTM D638/ISO 527	175	kg/cm²(MPa)[Lb/in²]
elongation	Break	ASTMD638	1.8	%
Bending modulus		ASTMD790	13500	Mpa
bending strength		ASTM D790/ISO 178	270	kg/cm²(MPa)[Lb/in²]
	bending strength		ASTM D-790	270	Mpa
	bending strength	bending strength		ASTMD790	270	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	265	°C
Flame retardant grade		UL 94	V-0
Linear coefficient of thermal expansion	TD:-30to90°C	ASTMD696	2.2E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:-30to90°C	ASTMD696	2.2E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation factor	1MHz	ASTMD150	2E-03
Dielectric strength	1.60mm	ASTMD149	16	KV/mm
Leakage Trace Index		ASTMD3638	170	V
Dielectric constant	1MHz	ASTMD150	4.00
Arc resistance		ASTMD495	125	sec
Volume resistivity		ASTMD257	1E+16	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Cantilever beam without notch impact strength		ASTMD256	600	J/m

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Scale	ASTMD785	100
Rockwell hardness	Rockwell hardness	R-Scale	ASTMD785	121

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.40mm	UL94	V-0

Basic performance	Test Condition	Test Method	Test Result	Unit
Water absorption rate		ASTM D-570	0.02	%
density		ASTM D-792	1.66	g/cm³

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.