PPS Torelina® A310MX04 TORAY JAPAN

204

Unit Price:
$5916 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
31MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant Glass fiber reinforced Mineral reinforcement High rigidity high strength High temperature resistan
Application Areas:Fiber grade
Color:--
Grade:Flame retardant enhanced grade

Technical Data Sheet

Physical properties	Test Method	Test Result	Unit
density	ASTM D792/ISO 1183	1.97
Molding shrinkage rate	ASTM D955	0.2	%
Water absorption rate 23 ℃/24h	ASTM D570/ISO 62	0.02	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Flow	东丽法	0.15	%
Shrinkage rate	Shrinkage rate	垂重方向	东丽法	0.55	%
Water absorption rate	(23°C,24hr)	ISO62	0.02	%
Flowing Long	320℃,98MPa,1mm厚	东丽法	90

Mechanical performance	Test Condition	Test Method	Test Result	Unit
abrasion		ASTM D-1044	70	mg/1000回
Limit PV value		东丽法	815	KJ/m
Curved elastic body		ASTM D-790	17.6	GPa
hardness		ASTM D-785	123	洛氏
Impact strength of simply supported beam without notch	23°C	ISO179/1eU	18	kJ/m²
Fracture strength		ASTM D-732	60
shear strength		ISO178	60	Mpa
Tensile strength		ASTM D-638	140	Mpa
friction coefficient	对钢	ASTM D-1894	0.30
Charpy Notched Impact Strength	23°C	ISO179/1eA	8.0	kJ/m²
impact strength	Notched23℃	ASTM D-256	90	J/m
impact strength	impact strength	Unnotched23℃	ASTM D-256	20	KJ/m
elongation at break		ASTM D638/ISO 527	0.8	%
elongation at break	elongation at break	23°C	ISO527-2	0.8	%
tensile strength		ASTM D638/ISO 527	130	kg/cm²(MPa)[Lb/in²]
	tensile strength	23°C	ISO527-2	130	Mpa
	tensile strength	tensile strength		ASTM D-638	1.2	%
Rockwell hardness		ASTM D785	123
Bending modulus		ASTM D790/ISO 178	22	kg/cm²(MPa)[Lb/in²]
Bending modulus	Bending modulus	23°C	ISO178	22000	Mpa
bending strength	23°C	ISO178	210	Mpa
	bending strength		ASTM D790/ISO 178	210	kg/cm²(MPa)[Lb/in²]
	bending strength	bending strength		ASTM D-790	200	Mpa
Charpy impact strength		ASTM D256/ISO 179	8	kg·cm/cm(J/M)ft·lb/in
Charpy impact strength	Charpy impact strength		ASTM D256/ISO 179	18	kg·cm/cm(J/M)ft·lb/in

Thermal performance	Test Condition	Test Method	Test Result	Unit
Combustibility		UL-94	V-0
Vicat softening temperature	Melting Temperature	ISO11357-3	278	°C
Combustibility (rate)		UL94	V-0
Hot deformation temperature		ASTM D648/ISO 75	>260	℃（℉）
	Hot deformation temperature	1.80MPaAnnealed	ISO75-2/Af	>260	°C
	Hot deformation temperature	Hot deformation temperature	1.82MPa	ASTM D-648	>260	°C
melting point			278	℃（℉）
Linear expansion coefficient		ASTM D696/ISO 11359	1.7	mm/mm.℃
Rongdian		DSC	278	°C
Coefficient of linear expansion	MD	ISO11359-2	1.7E-05	cm/cm/°C
Coefficient of linear expansion	Coefficient of linear expansion	TD	ISO11359-2	2.4E-05	cm/cm/°C
Line expansion coefficient	Flow	ASTM D-696	1.6
Line expansion coefficient	Line expansion coefficient	垂重方向	ASTM D-696	2.4

Electrical performance	Test Condition	Test Method	Test Result	Unit
Arc resistance W level		ASTM D-495	182	秒
Insulation strength		IEC60243-1	19	KV/mm
Volume resistance		IEC60093	1E+19	Ω.cm
permittivity	10	ASTM D-150	5.8
Induced positive connection	10	ASTM D-150	0.002
Inherent resistance of volume		ASTM D-257	10	Ω.m
Insulation breakdown voltage		ASTM D-149	15	MV/m
Dissipation factor	23°C	IEC60250	2E-03	1MHz
Dielectric constant		ASTM D150/IEC 60250	5
Dielectric constant	Dielectric constant	23°C	IEC60250	5.1	1MHz
Volume resistivity		ASTM D257/IEC 60093	1014	Ω.cm

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness		ISO2039-2	123	R

flammability	Test Condition	Test Method	Test Result	Unit
Fire rating		UL-94	0.36mm	V-0
	Fire rating		UL-94	0.74mm	V-0
		Fire rating		UL-94	1.50mm	V-0
			Fire rating		UL-94	3.00mm	V-0
			Fire rating	Fire rating		UL-94	2.00mm	V-0,5VA

Basic performance	Test Condition	Test Method	Test Result	Unit
Water absorption rate		ASTM D-570	0.02	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.