PPS Torelina® A604 TORAY JAPAN

236

Unit Price:
$6764 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
130MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan Glass fiber reinforced Flame retardant
Application Areas:Electrical field Electronic field Automotive sector sporting goods
Color:--
Grade:Injection grade

Technical Data Sheet

Physical properties	Test Method	Test Result	Unit
density	ASTM D792/ISO 1183	1.66
Molding shrinkage rate	ASTM D955	0.2	%
Water absorption rate 23 ℃/24h	ASTM D570/ISO 62	0.02	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:3.00mm2	内部方法	0.80	%
Shrinkage rate	Shrinkage rate	MD:3.00mm4	内部方法	0.20	%
Water absorption rate	23°C,24hr	ISO62	0.020	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Yield,23°C	ISO527-2	205	Mpa
Tensile strain	Break,23°C	ISO527-2	2.0	%
Bending stress	23°C	ISO178	300	Mpa
Taber abraser	1000Cycles	ISO9352	50.0	mg
shear strength	23°C	JISK7214	80.0	Mpa
Friction coefficient 4			0.24
elongation at break		ASTM D638/ISO 527	2	%
tensile strength		ASTM D638/ISO 527	205	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	122
Bending modulus		ASTM D790/ISO 178	14.5	kg/cm²(MPa)[Lb/in²]
Bending modulus	Bending modulus	23°C	ISO178	14500	Mpa
bending strength		ASTM D790/ISO 178	300	kg/cm²(MPa)[Lb/in²]
Charpy impact strength		ASTM D256/ISO 179	12	kg·cm/cm(J/M)ft·lb/in
Charpy impact strength	Charpy impact strength		ASTM D256/ISO 179	60	kg·cm/cm(J/M)ft·lb/in

Thermal performance	Test Condition	Test Method	Test Result	Unit
Combustibility (rate)		UL94	V-0
Hot deformation temperature		ASTM D648/ISO 75	>260	℃（℉）
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	260	°C
melting point			278	℃（℉）
Linear expansion coefficient		ASTM D696/ISO 11359	2.3	mm/mm.℃
Linear coefficient of thermal expansion	MD	ISO11359-2	2.3E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	3.5E-05	cm/cm/°C
Melting temperature		ISO11357-3	278	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric strength		IEC60243-1	24	KV/mm
Dielectric constant 6	23°C,1MHz	IEC60250	3.60
Dissipation factor 5	23°C,1MHz	IEC60250	2E-03
Dielectric constant		ASTM D150/IEC 60250	3.6
Volume resistivity		ASTM D257/IEC 60093	1014	Ω.cm
Volume resistivity	Volume resistivity		IEC60093	1E+16	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	60	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ISO2039-2	122

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.200mm	UL94	V-0

Supplementary Information	Test Condition	Test Method	Test Result	Unit
BarFlowLength6	320°C,1.00mm	内部方法	120	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.