PPS Torelina® A504X90 TORAY JAPAN

211

Unit Price:
$6257 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
70MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Chemical resistance Flame retardant Glass fiber reinforced High impact resistance High temperature resistan
Application Areas:Electrical components Automotive sector sporting goods small home appliances
Color:--
Grade:Injection grade

Technical Data Sheet

Physical properties	Test Method	Test Result	Unit
density	ASTM D792/ISO 1183	1.66
Molding shrinkage rate	ASTM D955	0.36	%
Water absorption rate 23 ℃/24h	ASTM D570/ISO 62	0.02	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:3.00mm2	内部方法	0.80	%
Shrinkage rate	Shrinkage rate	MD:3.00mm4	内部方法	0.20	%
Water absorption rate	23°C,24hr	ISO62	0.020	%
Mold shrinkage rate	Across Flow	TORAY	0.70	%
Mold shrinkage rate	Mold shrinkage rate	Flow	TORAY	0.20	%
Taber abrasion		ASTM D-D1044	50	mg/1000次
Friction coefficient/against iron		ASTM D-1894	0.25
Limit PV value		TORAY	815	KJ/m

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Elongation rate	23℃	ASTM D-638	3.6	%
Friction coefficient 4			0.25
compressive strength		ASTM D-732	80
shear strength	23°C	JISK7214	80.0	Mpa
Bending stress	23°C	ISO178	305	Mpa
Taber abraser	1000Cycles	ISO9352	50.0	mg
Tensile stress	Yield,23°C	ISO527-2	200	Mpa
Tensile strain	Break,23°C	ISO527-2	1.8	%
elongation at break		ASTM D638/ISO 527	1.8	%
tensile strength		ASTM D638/ISO 527	200	kg/cm²(MPa)[Lb/in²]
tensile strength	tensile strength	23℃	ASTM D-638	207	Mpa
Rockwell hardness		ASTM D-785	122	R
Rockwell hardness	Rockwell hardness		ASTM D785	122
Bending modulus		ASTM D790/ISO 178	15.5	kg/cm²(MPa)[Lb/in²]
	Bending modulus	23℃	ASTM D-790	13.3	GPa
	Bending modulus	Bending modulus	23°C	ISO178	15500	Mpa
bending strength		ASTM D790/ISO 178	305	kg/cm²(MPa)[Lb/in²]
bending strength	bending strength	23℃	ASTM D-790	275	Mpa
IZOD impact strength	Notched	ASTM D-256	130	J/m
IZOD impact strength	IZOD impact strength	Unnotched	ASTM D-256	55	KJ/m
Charpy impact strength		ASTM D256/ISO 179	11	kg·cm/cm(J/M)ft·lb/in
Charpy impact strength	Charpy impact strength		ASTM D256/ISO 179	55	kg·cm/cm(J/M)ft·lb/in

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion	MD	ISO11359-2	2.3E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO11359-2	3.1E-05	cm/cm/°C
Melting temperature		ISO11357-3	278	°C
Combustibility (rate)		UL94	V-0
Hot deformation temperature		ASTM D648/ISO 75	>260	℃（℉）
	Hot deformation temperature	1.82MPa	ASTM D-648	>260	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	260	°C
melting point		DSC	278	°C
melting point	melting point			278	℃（℉）
Thermal expansion coefficient	Flow	ASTM D-696	2.3
Thermal expansion coefficient	Thermal expansion coefficient	Across Flow	ASTM D-696	3.2

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistance		ASTM D-257	10	Ω.m
Dielectric strength		IEC60243-1	24	KV/mm
Dielectric strength	Dielectric strength		ASTM D-149	21	MV/m
Dielectric constant 6	23°C,1MHz	IEC60250	4.20
Arc resistance		ASTM D-495	127
Dissipation factor 5	23°C,1MHz	IEC60250	2E-03
loss factor	10	ASTM D-150	0.002
Dielectric constant		ASTM D150/IEC 60250	4.2
Dielectric constant	Dielectric constant	10	ASTM D-150	3.8
Volume resistivity		ASTM D257/IEC 60093	1014	Ω.cm
Volume resistivity	Volume resistivity		IEC60093	1E+16	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	55	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ISO2039-2	122

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.28mm	UL94	V-0

Basic performance	Test Condition	Test Method	Test Result	Unit
Water absorption rate	24hr,23℃于水中	ASTM D-570	0.02	%

Supplementary Information	Test Condition	Test Method	Test Result	Unit
BarFlowLength6	320°C,1.00mm	内部方法	135	mm

Other performance	Test Condition	Test Method	Test Result	Unit
Flowing Long	320℃,98MPa	TORAY	100

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.